Properties of Grouting Mortar Modified with Alunite/Bauxite/Gypsum Ternary System as Expansion Component
The ettringite results from alunite/bauxite and gypsum which has the characteristic of fast setting and volume expansion, so the main properties and microscopic structure of grouting material modified with alunite/bauxite and gypsum at different proportion were investigated. The results have shown that the grouting mortar modified with 7-20% content of bauxite/alunite/gypsum had the properties such as the setting time could be controlled below 1 hour, long-term expansion rate stabilized basically as 0.2%, compressive strength of 1, 3 and 14 days were more than 17 MPa, 31 MPa and 50 MPa, respectively; the pullout force of 1 meter sample at 14 days reached 87 kN. The micro-analyzing by using MIP, SEM and XRD showed that there were plenty of expansive crystals and tiny pore structures in harded paste which can exist steadily for a long term. The achievements will provide an important basis to application of cement-based grouting material as first-aid repairing.
Properties of Grouting Mortar Modified with Alunite/Bauxite/Gypsum Ternary System as Expansion Component
The ettringite results from alunite/bauxite and gypsum which has the characteristic of fast setting and volume expansion, so the main properties and microscopic structure of grouting material modified with alunite/bauxite and gypsum at different proportion were investigated. The results have shown that the grouting mortar modified with 7-20% content of bauxite/alunite/gypsum had the properties such as the setting time could be controlled below 1 hour, long-term expansion rate stabilized basically as 0.2%, compressive strength of 1, 3 and 14 days were more than 17 MPa, 31 MPa and 50 MPa, respectively; the pullout force of 1 meter sample at 14 days reached 87 kN. The micro-analyzing by using MIP, SEM and XRD showed that there were plenty of expansive crystals and tiny pore structures in harded paste which can exist steadily for a long term. The achievements will provide an important basis to application of cement-based grouting material as first-aid repairing.
Properties of Grouting Mortar Modified with Alunite/Bauxite/Gypsum Ternary System as Expansion Component
Advanced Materials Research ; 815 ; 839-844
07.10.2013
6 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Properties of cement-based bolt-grouting materials modified with alunite and gypsum
| Online Contents | 2016
Properties of Bolt-Grouting Mortar Modified with Mineral Bauxite by Chemical Activation
| Online Contents | 2016
Properties of Bolt-Grouting Mortar Modified with Mineral Bauxite by Chemical Activation
| Online Contents | 2016