Influence of Sulphate on the Moisture Movement of Calcium Silicate Brick Masonry Wall
This paper presents the behaviour of moisture movement of calcium silicate brick masonry walls exposed to sodium sulphate environment. The walls were exposed to three sodium sulphate conditions with sulphate concentrations of5%, 10% and 15%. For comparison, some walls were also exposed to dry and wet condition which acts as a control conditions. All specimens were prepared and cured under polythene sheet for 14 days in a controlled environmental room and maintained at relative humidity and temperature of 80 ± 5% and 25 ± 2°C, respectively. After the curing period, the specimens were exposed to sodium sulphate as well as drying and water exposures, during which moisture movement was measured and monitored for a period of up to 7 months. As a result, the moisture expansion was observed and recorded for all masonry wall specimens after exposed to the sulphate condition.
Influence of Sulphate on the Moisture Movement of Calcium Silicate Brick Masonry Wall
This paper presents the behaviour of moisture movement of calcium silicate brick masonry walls exposed to sodium sulphate environment. The walls were exposed to three sodium sulphate conditions with sulphate concentrations of5%, 10% and 15%. For comparison, some walls were also exposed to dry and wet condition which acts as a control conditions. All specimens were prepared and cured under polythene sheet for 14 days in a controlled environmental room and maintained at relative humidity and temperature of 80 ± 5% and 25 ± 2°C, respectively. After the curing period, the specimens were exposed to sodium sulphate as well as drying and water exposures, during which moisture movement was measured and monitored for a period of up to 7 months. As a result, the moisture expansion was observed and recorded for all masonry wall specimens after exposed to the sulphate condition.
Influence of Sulphate on the Moisture Movement of Calcium Silicate Brick Masonry Wall
Advanced Materials Research ; 133-134 ; 201-204
19.10.2010
4 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Influence of Sulphate on the Moisture Movement of Calcium Silicate Brick Masonry Wall
| British Library Conference Proceedings | 2010
Elasticity of Calcium Silicate Brick Masonry Wall Due to Sulphate Attack
| British Library Conference Proceedings | 2010
Elasticity of Calcium Silicate Brick Masonry Wall Due to Sulphate Attack
| Trans Tech Publications | 2010
Moisture movement of fired clay brick masonry wall under sulphate environment
| British Library Conference Proceedings | 2010
Bond strength in calcium silicate brick masonry
| British Library Conference Proceedings | 2004