Shrinkage Performance and Cracking Resistance Mechanism of Rubberized Lightweight Aggregate Concrete with Polymer
To improve the cracking resistance of lightweight aggregate concrete, rubber particles and polymer were added. Experimental results showed that the shrinkage rate increased when rubber particles were added into lightweight aggregate concrete, but when polymer was mixed, the shrinkage rate decreased dramatically. Microstructure analysis indicated that the interface transition zone (ITZ) influenced the shrinkage performance of rubberized lightweight aggregate concrete with polymer directly; the ITZ bondage between rubber particles and cement matrix was very poor and the restriction to shrinkage was weak, which were the main reasons for the increase of shrinkage rate of rubberized lightweight aggregate concrete; when polymer was mixed into the concrete, the hole and ITZ structure of concrete were improved, which made the strain energy absorbing function of rubber particles can be exerted entirely and the flexibility of ITZ was boosted, thereby the shrinkage performance and cracking resistance of lightweight aggregate concrete were improved.
Shrinkage Performance and Cracking Resistance Mechanism of Rubberized Lightweight Aggregate Concrete with Polymer
To improve the cracking resistance of lightweight aggregate concrete, rubber particles and polymer were added. Experimental results showed that the shrinkage rate increased when rubber particles were added into lightweight aggregate concrete, but when polymer was mixed, the shrinkage rate decreased dramatically. Microstructure analysis indicated that the interface transition zone (ITZ) influenced the shrinkage performance of rubberized lightweight aggregate concrete with polymer directly; the ITZ bondage between rubber particles and cement matrix was very poor and the restriction to shrinkage was weak, which were the main reasons for the increase of shrinkage rate of rubberized lightweight aggregate concrete; when polymer was mixed into the concrete, the hole and ITZ structure of concrete were improved, which made the strain energy absorbing function of rubber particles can be exerted entirely and the flexibility of ITZ was boosted, thereby the shrinkage performance and cracking resistance of lightweight aggregate concrete were improved.
Shrinkage Performance and Cracking Resistance Mechanism of Rubberized Lightweight Aggregate Concrete with Polymer
Key Engineering Materials ; 385-387 ; 817-820
02.07.2008
4 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
| British Library Online Contents | 2008
Mechanical properties of rubberized lightweight aggregate concrete
| British Library Online Contents | 2017
Mechanical properties of rubberized lightweight aggregate concrete
| Online Contents | 2017
Compressive Properties of Rubberized Lightweight Aggregate Concrete
| British Library Conference Proceedings | 2007
Mechanical properties of rubberized lightweight aggregate concrete
| British Library Online Contents | 2017