Effect of Ferronickel Slag as Cementitious Material on Strength of Mortar
In this work, the performance of mortar made with ferronickel slag (FNS) as cement replacement was investigated. The granulated FNS was ground to obtain a fineness higher than cement. To assess the performance of FNS in fresh and hardened mortar, the workability, flexural, and compressive strength were experimentally assessed. Based on the results obtained, the fluidity of mortar increased with increasing FNS content. It was found that FNS did not promote the compressive strength of mortar in the early days of curing, but at longer curing times the FNS starts to react. Although there is a decrease in flexural strength of mortar containing FNS, this result tends to be better than the compressive strength performance. The presence of FNS in mortar increased the porosity.
Effect of Ferronickel Slag as Cementitious Material on Strength of Mortar
In this work, the performance of mortar made with ferronickel slag (FNS) as cement replacement was investigated. The granulated FNS was ground to obtain a fineness higher than cement. To assess the performance of FNS in fresh and hardened mortar, the workability, flexural, and compressive strength were experimentally assessed. Based on the results obtained, the fluidity of mortar increased with increasing FNS content. It was found that FNS did not promote the compressive strength of mortar in the early days of curing, but at longer curing times the FNS starts to react. Although there is a decrease in flexural strength of mortar containing FNS, this result tends to be better than the compressive strength performance. The presence of FNS in mortar increased the porosity.
Effect of Ferronickel Slag as Cementitious Material on Strength of Mortar
Key Engineering Materials ; 931 ; 213-218
10.10.2022
6 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Mortar composition containing ferronickel slag as binder
Europäisches Patentamt | 2021
Mortar composition containing ferronickel slag as binder
| Europäisches Patentamt | 2021
Mortar Composition using Ferronickel Slag Powder and Admixtures
| Europäisches Patentamt | 2021
SELF-COMPACTING CONCRETE WITH GROUND FERRONICKEL SLAG AS SUPPLEMENTARY CEMENTITIOUS MATERIAL
| TIBKAT | 2023