Evaluation of Shrinkage Resulted Cracking of High Strength Calcium Sulfoaluminate Cement Concrete with Impact of Internal Curing
In this paper, restrained ring test and shrinkage test are carried on three kinds of concrete—high-strength portland cement concrete, high-strength calcium sulfoaluminate cement concrete and high-strength calcium sulfoaluminate cement concrete with internal curing in order to evaluate the shrinkage induced cracking performance of the concretes. The experimental results show that calcium sulfoaluminate cement concrete exhibits lower shrinkage caused by surface drying comparing to portland cement concrete. Internal curing can eliminate most of the autogenous shrinkage of concrete. In the ring test, the latter two concrete did not crack during the whole test history—42 days, while high-strength portland cement concrete cracked at the 13th day after casting. High strength calcium sulfoaluminate cement concrete exhibits better anti-cracking ability than the high strength portland cement concrete with the same strength grade.
Evaluation of Shrinkage Resulted Cracking of High Strength Calcium Sulfoaluminate Cement Concrete with Impact of Internal Curing
In this paper, restrained ring test and shrinkage test are carried on three kinds of concrete—high-strength portland cement concrete, high-strength calcium sulfoaluminate cement concrete and high-strength calcium sulfoaluminate cement concrete with internal curing in order to evaluate the shrinkage induced cracking performance of the concretes. The experimental results show that calcium sulfoaluminate cement concrete exhibits lower shrinkage caused by surface drying comparing to portland cement concrete. Internal curing can eliminate most of the autogenous shrinkage of concrete. In the ring test, the latter two concrete did not crack during the whole test history—42 days, while high-strength portland cement concrete cracked at the 13th day after casting. High strength calcium sulfoaluminate cement concrete exhibits better anti-cracking ability than the high strength portland cement concrete with the same strength grade.
Evaluation of Shrinkage Resulted Cracking of High Strength Calcium Sulfoaluminate Cement Concrete with Impact of Internal Curing
Key Engineering Materials ; 629-630 ; 144-149
01.10.2014
6 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
| British Library Conference Proceedings | 2015
Shrinkage and creep of high-performance concrete based on calcium sulfoaluminate cement
| BASE | 2019
Shrinkage and Cracking of Cement Composites Containing Internal Curing Stuff
| British Library Conference Proceedings | 2011