Effect of Aging on Microstructure and Performance after Superplastic Deformation of Fine Grained 1420 Al-Li Alloy
Superplastic forming (SPF) is an important process for forming fine grained 1420 Al-Li alloy. However, the mechanical properties will be decreased after deforming at high temperature. How to obtain the optimize relationship of strength and ductility after SPF is one of the key problems for the process. In this paper, a set of artificial aging tests including single and two-step aging were carried out, which are the typical strengthening process for Al-Li alloy. Based on experimental results, strength and elongation were studied by means of tensile tests at room temperature, and the effect of aging processes on mechanical properties was analyzed. Finally, the microstructures fore and after aging were examined by OM and TEM, and the strengthening mechanism of 1420 Al-Li alloy was further studied. It is found that artificial aging especially two-step aging can increase mechanical properties of post-SPF material obviously, and δ (Al3Li) is the primary strengthening phase.
Effect of Aging on Microstructure and Performance after Superplastic Deformation of Fine Grained 1420 Al-Li Alloy
Superplastic forming (SPF) is an important process for forming fine grained 1420 Al-Li alloy. However, the mechanical properties will be decreased after deforming at high temperature. How to obtain the optimize relationship of strength and ductility after SPF is one of the key problems for the process. In this paper, a set of artificial aging tests including single and two-step aging were carried out, which are the typical strengthening process for Al-Li alloy. Based on experimental results, strength and elongation were studied by means of tensile tests at room temperature, and the effect of aging processes on mechanical properties was analyzed. Finally, the microstructures fore and after aging were examined by OM and TEM, and the strengthening mechanism of 1420 Al-Li alloy was further studied. It is found that artificial aging especially two-step aging can increase mechanical properties of post-SPF material obviously, and δ (Al3Li) is the primary strengthening phase.
Effect of Aging on Microstructure and Performance after Superplastic Deformation of Fine Grained 1420 Al-Li Alloy
Advanced Materials Research ; 936 ; 1647-1652
30.06.2014
6 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Cavitation Behavior of Fine-Grained 1420 Al-Li Alloy during Superplastic Deformation
| British Library Online Contents | 2007
Superplastic Deformation and Microstructure Evolution of Friction Stir Weld of 1420 Al-Li Alloy
| British Library Online Contents | 2005
Superplastic behaviour and microstructure evolution of a fine-grained TA15 titanium alloy
| British Library Online Contents | 2009
Superplastic deformation of a fine-grained Zn-0.3wt.%Al alloy at room temperature
| British Library Online Contents | 2001
Superplastic elongation characteristic of fine grained magnesium alloy ZK60
| British Library Online Contents | 2010