Corrosion of reinforcement in concrete : the effectiveness of organic corrosion inhibitors
Includes bibliographical references. Reinforcement corrosion in concrete has presented engineers with the challenge of finding ways of prolonging the service life of structures built in aggressive environments. One method of increasing the durability of concrete in aggressive environments is the use of corrosion inhibitors. In this work, two organic corrosion inhibitors were tested to observe their effectiveness in decreasing the rate of corrosion or delaying the onset of corrosion. One of the inhibitors was a migrating corrosion inhibitor while the other was an admixed inhibitor. The corrosion rate of reinforcement in concrete specimens used in this evaluation, was measured using the Linear Polarisation Resistance method. The performance of the admixed inhibitor was also measured in aqueous phase tests. Results of the tests conducted indicate that the admixed inhibitor does delay the onset of corrosion. The Mel caused short to medium term inhibition when the chloride concentration was less than 1.5%.
Corrosion of reinforcement in concrete : the effectiveness of organic corrosion inhibitors
Includes bibliographical references. Reinforcement corrosion in concrete has presented engineers with the challenge of finding ways of prolonging the service life of structures built in aggressive environments. One method of increasing the durability of concrete in aggressive environments is the use of corrosion inhibitors. In this work, two organic corrosion inhibitors were tested to observe their effectiveness in decreasing the rate of corrosion or delaying the onset of corrosion. One of the inhibitors was a migrating corrosion inhibitor while the other was an admixed inhibitor. The corrosion rate of reinforcement in concrete specimens used in this evaluation, was measured using the Linear Polarisation Resistance method. The performance of the admixed inhibitor was also measured in aqueous phase tests. Results of the tests conducted indicate that the admixed inhibitor does delay the onset of corrosion. The Mel caused short to medium term inhibition when the chloride concentration was less than 1.5%.
Corrosion of reinforcement in concrete : the effectiveness of organic corrosion inhibitors
Rylands, Thaabit (Autor:in)
2014
1 Online-Ressource
Hochschulschrift
Elektronische Ressource
Englisch
Corrosion of reinforcement in concrete : the effectiveness of organic corrosion inhibitors
| BASE | 1999
Effectiveness of corrosion inhibitors in contaminated concrete
| Online Contents | 2003
Effectiveness of concrete inhibitors in retarding rebar corrosion
| Online Contents | 2002
Corrosion and concrete reinforcement
| British Library Online Contents | 2001