Carbonation behaviour of concretes with alternative binders at different CO2 concentrations
AbstractIn order to reduce CO2 emissions in the construction sector, alternative binders are attracting more and more attention. Whether these alternative binders contain a lower clinker‐cement ratio or no Portland cement clinker at all, to be truly sustainable they must not compromise durability and must therefore be durable.The progress of carbonation and the associated reduction of the pH value have a major influence on the corrosion protection of steel reinforcement, especially as such “low carbon” concretes are typically less resistant against CO2 exposure. Previous research has shown that accelerated tests at elevated CO2 concentrations can lead to altered carbonation behavior, especially in systems low in Ca(OH)2.In this study, hydration products and carbonation resistance of various alternative cements and binders, such as composite cements with calcined clays or modified steel slag, alkali‐activated materials, C$SMA cement and a C‐S‐H binder were investigated. The carbonation was studied on mortar samples stored in three different CO2 concentrations ‐ atmospheric storage (∼0.04 vol.%), 0.3 vol.% and 1.0 vol.% CO2. It was found that the binders can be divided into three clusters on the basis of their hydration products and w/CaO or w/(CaO + MgOeq + Na2Oeq + K2Oeq) ratios, which in turn provide information on the carbonation behavior. For each cluster a different CO2 concentration can be recommended to achieve a realistic carbonation behavior in accelerated test procedures.
Carbonation behaviour of concretes with alternative binders at different CO2 concentrations
AbstractIn order to reduce CO2 emissions in the construction sector, alternative binders are attracting more and more attention. Whether these alternative binders contain a lower clinker‐cement ratio or no Portland cement clinker at all, to be truly sustainable they must not compromise durability and must therefore be durable.The progress of carbonation and the associated reduction of the pH value have a major influence on the corrosion protection of steel reinforcement, especially as such “low carbon” concretes are typically less resistant against CO2 exposure. Previous research has shown that accelerated tests at elevated CO2 concentrations can lead to altered carbonation behavior, especially in systems low in Ca(OH)2.In this study, hydration products and carbonation resistance of various alternative cements and binders, such as composite cements with calcined clays or modified steel slag, alkali‐activated materials, C$SMA cement and a C‐S‐H binder were investigated. The carbonation was studied on mortar samples stored in three different CO2 concentrations ‐ atmospheric storage (∼0.04 vol.%), 0.3 vol.% and 1.0 vol.% CO2. It was found that the binders can be divided into three clusters on the basis of their hydration products and w/CaO or w/(CaO + MgOeq + Na2Oeq + K2Oeq) ratios, which in turn provide information on the carbonation behavior. For each cluster a different CO2 concentration can be recommended to achieve a realistic carbonation behavior in accelerated test procedures.
Carbonation behaviour of concretes with alternative binders at different CO2 concentrations
ce papers
Kraft, Bettina (Autor:in) / Müller, Matthias (Autor:in) / Achenbach, Rebecca (Autor:in) / Ludwig, Horst‐Michael (Autor:in) / Raupach, Michael (Autor:in)
ce/papers ; 6 ; 1334-1341
01.12.2023
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
| Springer Verlag | 2011
Road concretes and protective concretes with hydrocarbon binders
| Engineering Index Backfile | 1948
Carbonation of self compacting concretes produced with different materials
| British Library Conference Proceedings | 2007