Shear behavior of concrete beams reinforced exclusively with longitudinal glass fiber reinforced polymer bars: Experimental research
This paper aims to investigate the shear failure mechanisms in beams exclusively reinforced with longitudinal glass fiber reinforced polymer bars and to propose a design‐based approach to predict the shear capacity of this type of beams. An experimental program composed of seven T cross section shaped concrete beams was executed to analyze the influence of the flexural reinforcement configuration on the shear capacity and deformability of the beams. Three values of the flexural reinforcement ratio (ρl), 1%, 1.4%, and 1.80% were adopted. Digital image correlation technique was used to better capture and analyze the cracking process up to the formation of the shear failure crack. Test results indicated that the shear capacity was not dependent of ρl up to a limit of around 1.4%, but a tendency of the shear capacity to increase with ρl was registered above this limit due to a more pronounced favorable contribution of aggregate interlock and dowel effect.
Shear behavior of concrete beams reinforced exclusively with longitudinal glass fiber reinforced polymer bars: Experimental research
This paper aims to investigate the shear failure mechanisms in beams exclusively reinforced with longitudinal glass fiber reinforced polymer bars and to propose a design‐based approach to predict the shear capacity of this type of beams. An experimental program composed of seven T cross section shaped concrete beams was executed to analyze the influence of the flexural reinforcement configuration on the shear capacity and deformability of the beams. Three values of the flexural reinforcement ratio (ρl), 1%, 1.4%, and 1.80% were adopted. Digital image correlation technique was used to better capture and analyze the cracking process up to the formation of the shear failure crack. Test results indicated that the shear capacity was not dependent of ρl up to a limit of around 1.4%, but a tendency of the shear capacity to increase with ρl was registered above this limit due to a more pronounced favorable contribution of aggregate interlock and dowel effect.
Shear behavior of concrete beams reinforced exclusively with longitudinal glass fiber reinforced polymer bars: Experimental research
Kaszubska, Monika (Autor:in) / Kotynia, Renata (Autor:in) / Barros, Joaquim A. O. (Autor:in) / Baghi, Hadi (Autor:in)
Structural Concrete ; 19 ; 152-161
01.02.2018
10 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Shear Behavior of Geopolymer Concrete Beams Reinforced with Glass Fiber-Reinforced Polymer Bars
| Online Contents | 2017