Mechanisms of Fabric Reinforcement of Cement Matrices
10.1002/best.200490116.abs
The present paper discusses the mechanisms involve in fabric‐cement composites focusing on the effects of fabric geometry and the properties of the yarns. It was found that the geometry of a given fabric could enhance the bonding and enable one to obtain strain hardening behavior from low modulus yarn fabrics, due to the special shape of the yarn induced by the fabric. On the other hand, variations of the geometry in a fabric could drastically reduce the efficiency, resulting in a lower strengthening effect of the yarns in the fabric, relative to single yarns not in a fabric form. Therefore, in cement composites the fabrics can not be viewed simply as a means for holding together continuous yarns to be readily placed in the matrix, as is the case in composites with polymer matrix.
Mechanismen von Textilbewehrtem Beton
Einfluß der Gewebegeometrie und Garneigenschaften
Der Beitrag beschreibt die Mechanismen in zementgebundenen Verbundwerkstoffen mit textiler Bewehrung mit Schwerpunkt auf dem Einfluß der Geometrie der Textilien und der Eigenschaften der Garne. Es hat sich gezeigt, daß die Geometrie den Verbund verbessern kann und dafür sorgt, daß man ein günstiges Tragverhalten bei Textilien aus niedermoduligen Garnen aufgrund der speziellen Form der Garne im Textil erhält. Andererseits können Variationen in der Gewebegeometrie die Wirksamkeit der Bewehrung stark reduzieren, was sich in einer geringeren Verstärkungswirkung des Gewebes im Vergleich zum Einzelgarn ausdrückt. Daraus erkennt man, daß bei Betonbauteilen die textile Struktur nicht nur dem Zusammenhalten der Bewehrungsfasern für einen einfachen Einbau dient, wie das bei faserverstärkten Kunststoffen der Fall ist.
Mechanisms of Fabric Reinforcement of Cement Matrices
10.1002/best.200490116.abs
The present paper discusses the mechanisms involve in fabric‐cement composites focusing on the effects of fabric geometry and the properties of the yarns. It was found that the geometry of a given fabric could enhance the bonding and enable one to obtain strain hardening behavior from low modulus yarn fabrics, due to the special shape of the yarn induced by the fabric. On the other hand, variations of the geometry in a fabric could drastically reduce the efficiency, resulting in a lower strengthening effect of the yarns in the fabric, relative to single yarns not in a fabric form. Therefore, in cement composites the fabrics can not be viewed simply as a means for holding together continuous yarns to be readily placed in the matrix, as is the case in composites with polymer matrix.
Mechanismen von Textilbewehrtem Beton
Einfluß der Gewebegeometrie und Garneigenschaften
Der Beitrag beschreibt die Mechanismen in zementgebundenen Verbundwerkstoffen mit textiler Bewehrung mit Schwerpunkt auf dem Einfluß der Geometrie der Textilien und der Eigenschaften der Garne. Es hat sich gezeigt, daß die Geometrie den Verbund verbessern kann und dafür sorgt, daß man ein günstiges Tragverhalten bei Textilien aus niedermoduligen Garnen aufgrund der speziellen Form der Garne im Textil erhält. Andererseits können Variationen in der Gewebegeometrie die Wirksamkeit der Bewehrung stark reduzieren, was sich in einer geringeren Verstärkungswirkung des Gewebes im Vergleich zum Einzelgarn ausdrückt. Daraus erkennt man, daß bei Betonbauteilen die textile Struktur nicht nur dem Zusammenhalten der Bewehrungsfasern für einen einfachen Einbau dient, wie das bei faserverstärkten Kunststoffen der Fall ist.
Mechanisms of Fabric Reinforcement of Cement Matrices
Peled, Alva (Autor:in) / Bentur, Arnon (Autor:in)
Beton‐ und Stahlbetonbau ; 99 ; 456-459
01.06.2004
4 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Mechanisms of Fabric Reinforcement of Cement Matrices
| Online Contents | 2004
Woven fabric reinforcement of cement matrix
| Elsevier | 1993