    Effect of polarization on crack initiation and dislocation behaviour near the surface of A537 steel during low cycle corrosion fatigue in 3.5% NaCl solution

    New search for: Wang, J. Q.
    New search for: Li, J.
    New search for: Ke, W.

    Access

    Access via TIB
    Check availability in my library
    Order at Subito €

    Access

    Access via TIB
    Check availability in my library
    Order at Subito €

    Page navigation

    Document information
    Similar titles

    Export, share and cite

    Effect of polarization on crack initiation and dislocation behaviour near the surface of A537 steel during low cycle corrosion fatigue in 3.5% NaCl solution

    New search for: Wang, J. Q.
    New search for: Li, J.
    New search for: Ke, W.

    Access

    Access via TIB
    Check availability in my library
    Order at Subito €

    Effect of polarization on crack initiation and dislocation behaviour near the surface of A537 steel during low cycle corrosion fatigue in 3.5% NaCl solution

    New search for: Wang, J. Q.
    New search for: Li, J.
    New search for: Ke, W.

    Access

    Access via TIB
    Check availability in my library
    Order at Subito €

    Access

    Access via TIB
    Check availability in my library
    Order at Subito €

    Page navigation

    Document information
    Similar titles

    Export, share and cite

    Document information
    Title:

    Effect of polarization on crack initiation and dislocation behaviour near the surface of A537 steel during low cycle corrosion fatigue in 3.5% NaCl solution

    Contributors:

    Wang, J. Q. (author) / Li, J. (author) / Ke, W. (author)

    Published in:

    JOURNAL OF MATERIALS SCIENCE LETTERS ; 17 ; 345-348

    Publication date:

    1998-01-01

    Size:

    4 pages

    ISSN:

    0261-8028

    Type of media:

    Article (Journal)

    Type of material:

    Print

    Language:

    English

    Classification:

    DDC:  620.11

    © Metadata Copyright the British Library Board and other contributors. All rights reserved.

    Similar titles

    Crack growth retardation of single overload for A537 steel in a 3.5% NaCl solution under cathodic potential and free corrosion condition

    Xuejun, W. / Jin, L. / Wei, K. | British Library Online Contents | 1998

    Anisotropic 3D growth of corrosion pits initiated at MnS inclusions for A537 steel during corrosion fatigue

    Ma, J. / Zhang, B. / Wang, J. et al. | British Library Online Contents | 2010

    Stress corrosion cracking of A537 steel in simulated marine environments

    Du, X.S. / Su, Y.J. / Li, J.X. et al. | British Library Online Contents | 2012

    Dislocation Dipole Models for Fatigue Crack Initiation

    T. Mura / K. Tanaka | NTIS | 1981

    Corrosion Fatigue Crack Propagation Behavior of 2205 Duplex Stainless Steel in NaCl Solution

    Yang, Bin / Chen, Ji / Geng, Yue | British Library Online Contents | 2017

    Back to top