Flaking failure originating from a single surface crack in silicon nitride under rolling contact fatigue
Flaking failure originating from a single surface crack in silicon nitride under rolling contact fatigue
Flaking failure originating from a single surface crack in silicon nitride under rolling contact fatigue
KIDA, K. (author) / SAITO, M. (author) / KITAMURA, K. (author)
FATIGUE AND FRACTURE OF ENGINEERING MATERIALS AND STRUCTURES ; 28 ; 1087-1097
2005-01-01
11 pages
Article (Journal)
English
DDC:
620.1123
© Metadata Copyright the British Library Board and other contributors. All rights reserved.
Flaking failures originating from microholes of bearings under rolling contact fatigue:
| British Library Online Contents | 2006
| British Library Online Contents | 2006
Flaking failure in rolling contact fatigue caused by indentations on mating surface (I)
| British Library Online Contents | 2002
Flaking failure in rolling contact fatigue caused by indentations on mating surface (III)
| British Library Online Contents | 2002
Flaking failure in rolling contact fatigue caused by indentations on mating surface (II)
| British Library Online Contents | 2002