Separation of bulk and contact interface degradation in thin film silicon solar cells
The use of current injection and light exposure is shown to distinguish the impact of degradation in the contact, and intrinsic regions of a-Si:H solar cells, respectively. The drop in the maximum power conversion capability of the cell after light exposure is a consequence of an increase of dangling bonds in the intrinsic layer of the cell due to the Staebler-Wronksi effect. This has a detrimental effect on short circuit current, open circuit voltage, and fill factor. On the other hand, injected current increases the open circuit voltage and greatly reduces the fill factor without affecting the short circuit current, which is attributed to an increase of defects in the p-layer. A clear distinction from both degradation mechanisms is observed from evolution of the ideality factor m of the main junction, and the ideality factor n of the ZnO/a-Si:H(p) interface. A back-to-back diode model of a solar cell that considers the effect of non-ideal contacts, where a high value of n represents an increased tunneling transport at the contact interface, can effectively address the separation of damage in the two regions.
Separation of bulk and contact interface degradation in thin film silicon solar cells
The use of current injection and light exposure is shown to distinguish the impact of degradation in the contact, and intrinsic regions of a-Si:H solar cells, respectively. The drop in the maximum power conversion capability of the cell after light exposure is a consequence of an increase of dangling bonds in the intrinsic layer of the cell due to the Staebler-Wronksi effect. This has a detrimental effect on short circuit current, open circuit voltage, and fill factor. On the other hand, injected current increases the open circuit voltage and greatly reduces the fill factor without affecting the short circuit current, which is attributed to an increase of defects in the p-layer. A clear distinction from both degradation mechanisms is observed from evolution of the ideality factor m of the main junction, and the ideality factor n of the ZnO/a-Si:H(p) interface. A back-to-back diode model of a solar cell that considers the effect of non-ideal contacts, where a high value of n represents an increased tunneling transport at the contact interface, can effectively address the separation of damage in the two regions.
Separation of bulk and contact interface degradation in thin film silicon solar cells
Corpus-Mendoza, Asiel N. (author) / De Souza, M. M. (author) / Hamelmann, Frank (author)
2015-11-01
10 pages
Article (Journal)
Electronic Resource
English
Coloured Silicon and Apollo Thin Film Solar Cells
| British Library Conference Proceedings | 1996
Amorphous Silicon, Microcrystalline Silicon, and Thin-Film Polycrystalline Silicon Solar Cells
| British Library Online Contents | 2007
Crystalline Silicon Thin-Film Solar Cells on Silicon Nitride Ceramic Substrates
| British Library Online Contents | 2001
Progress and limitations of thin-film silicon solar cells
| British Library Online Contents | 2018
| British Library Online Contents | 2016