Improved Method for Bonding CFRP Overlays to Steel for Fatigue Repair
Experiments and computer simulations were carried out at the University of Kansas to investigate the use of composite materials for strengthening and repair of fatigue-vulnerable steel bridges. Prefabricated CFRP overlays were attached to welded coverplate specimens using a layer of epoxy resin. The specimens were then subjected to three-point bending under cyclic loading at a constant stress range. Early tests showed that bonding CFRP overlays to steel was an effective method to reduce the stress demand in areas susceptible to fatigue damage, and that this strengthening method could lead to substantial increases in crack initiation life. Fatigue tests also showed that maintaining the bond between the CFRP overlays and the steel was the most critical factor in the effectiveness of this strengthening technique. It was observed that the presence of a layer of breather fabric embedded within the layer of epoxy resin was the most important parameter affecting bond behavior under fatigue loading. This paper describes monotonic and fatigue tests carried out to evaluate the effect of the presence of breather fabric and thickness of the resin layer on bond strength and on the performance of the resin layer under fatigue loading. It was found that the mode of failure of the resin under monotonic and fatigue loading changed significantly due to the presence of the breather cloth. Although the presence of breather cloth had a negligible effect on the bond strength of thin resin layers, its effect on strength increased with the thickness of the resin layer. It was also found that the presence of the breather fabric had a very significant effect on the post-peak behavior of monotonic tests, which partially explains its beneficial effect on behavior under fatigue loading.
Improved Method for Bonding CFRP Overlays to Steel for Fatigue Repair
Experiments and computer simulations were carried out at the University of Kansas to investigate the use of composite materials for strengthening and repair of fatigue-vulnerable steel bridges. Prefabricated CFRP overlays were attached to welded coverplate specimens using a layer of epoxy resin. The specimens were then subjected to three-point bending under cyclic loading at a constant stress range. Early tests showed that bonding CFRP overlays to steel was an effective method to reduce the stress demand in areas susceptible to fatigue damage, and that this strengthening method could lead to substantial increases in crack initiation life. Fatigue tests also showed that maintaining the bond between the CFRP overlays and the steel was the most critical factor in the effectiveness of this strengthening technique. It was observed that the presence of a layer of breather fabric embedded within the layer of epoxy resin was the most important parameter affecting bond behavior under fatigue loading. This paper describes monotonic and fatigue tests carried out to evaluate the effect of the presence of breather fabric and thickness of the resin layer on bond strength and on the performance of the resin layer under fatigue loading. It was found that the mode of failure of the resin under monotonic and fatigue loading changed significantly due to the presence of the breather cloth. Although the presence of breather cloth had a negligible effect on the bond strength of thin resin layers, its effect on strength increased with the thickness of the resin layer. It was also found that the presence of the breather fabric had a very significant effect on the post-peak behavior of monotonic tests, which partially explains its beneficial effect on behavior under fatigue loading.
Improved Method for Bonding CFRP Overlays to Steel for Fatigue Repair
Alemdar, Fatih (author) / Matamoros, Adolfo B. (author) / Bennett, Caroline R. (author) / Barrett-Gonzalez, Ron (author) / Rolfe, Stanley T. (author)
Structures Congress 2011 ; 2011 ; Las Vegas, Nevada, United States
Structures Congress 2011 ; 133-144
2011-04-13
Conference paper
Electronic Resource
English
Improved Method for Bonding CFRP Overlays to Steel for Fatigue Repair
| British Library Conference Proceedings | 2011
Use of CFRP Overlays to Repair Fatigue Damage in Steel Plates under Tension Loading
| British Library Online Contents | 2014
Use of CFRP Overlays to Strengthen Welded Connections under Fatigue Loading
| Online Contents | 2012