PENINGKATAN KUAT TEKAN BETON GEOPOLIMER DENGAN MENGGUNAKAN VARIASI ABU CANGKANG TELUR BEBEK MELALUI PROSES PENGOVENAN
The objective of this research is to know the increase of compressive strength value of geopolymer concrete using duck egg duck ash with mixture of sodium silicate and sodium hydroxide at variation 0%, 80%, 90% and 100% at 7 days with heating specimen and control concrete room temperature. Ash duck egg shell used is burnt waste with temperatures reaching 800 ° C for ± 6 hours using ceramic burning oven. This study uses cylindrical test object with diameter 10 cm and height 20 cm with the quality of plan is fc '20 MPa. Testing of compressive strength of geopolymer concrete using Crushing Test Machine tool. In this purpose, the compressive strength of the geopolymer concrete produced by the concrete test object on variations 0%; 80%; 90%; and 100% ie 0 MPa; 6,32 MPa; 8,57 MPa; and 14,01MPa, while the concrete test object No concrete compressive strength was applied on variations of 0%; 80%; 90%; and 100% ie 7,64 MPa; 4,84MPa; 5,77MPa; and 6.19MPa. It can be seen that the maximum average compressive strength value is present in the 100% variation with the tested object being tested at 83°C first.
PENINGKATAN KUAT TEKAN BETON GEOPOLIMER DENGAN MENGGUNAKAN VARIASI ABU CANGKANG TELUR BEBEK MELALUI PROSES PENGOVENAN
The objective of this research is to know the increase of compressive strength value of geopolymer concrete using duck egg duck ash with mixture of sodium silicate and sodium hydroxide at variation 0%, 80%, 90% and 100% at 7 days with heating specimen and control concrete room temperature. Ash duck egg shell used is burnt waste with temperatures reaching 800 ° C for ± 6 hours using ceramic burning oven. This study uses cylindrical test object with diameter 10 cm and height 20 cm with the quality of plan is fc '20 MPa. Testing of compressive strength of geopolymer concrete using Crushing Test Machine tool. In this purpose, the compressive strength of the geopolymer concrete produced by the concrete test object on variations 0%; 80%; 90%; and 100% ie 0 MPa; 6,32 MPa; 8,57 MPa; and 14,01MPa, while the concrete test object No concrete compressive strength was applied on variations of 0%; 80%; 90%; and 100% ie 7,64 MPa; 4,84MPa; 5,77MPa; and 6.19MPa. It can be seen that the maximum average compressive strength value is present in the 100% variation with the tested object being tested at 83°C first.
PENINGKATAN KUAT TEKAN BETON GEOPOLIMER DENGAN MENGGUNAKAN VARIASI ABU CANGKANG TELUR BEBEK MELALUI PROSES PENGOVENAN
Anastasia, Kinanti (author) / Prihantono, Prihantono (author) / Anisah, Anisah (author)
2020-01-02
doi:10.21009/jmenara.v15i1.18127
Menara: Jurnal Teknik Sipil; Vol 15 No 1 (2020): Menara: Jurnal Teknik Sipil; 23 - 29 ; 2622-5549 ; 1907-4360
Article (Journal)
Electronic Resource
English
DDC:
690
Pemanfaatan Abu Serabut Kelapa dan Serbuk Cangkang Telur Terhadap Kuat Tekan Beton
| BASE | 2023
PENGARUH CANGKANG TELUR AYAM SEBAGAI SUBSTITUSI SEMEN TERHADAP KUAT TEKAN BETON ( 1-6 )
| BASE | 2020