Lithuanian quarry aggregates concrete effects of alkaline corrosion tests
Aggregate alkaline corrosion of cement in concrete is going to respond in sodium and potassium hydroxide (lye) with active SiO2 found in some aggregates. During this reaction, the concrete has resulted in significant internal stresses which cause deformation of the concrete, cracking and disintegration. The reaction is slow and concrete signs of decomposition appear only after a few months or years. The study used two different aggregates quarries. Studies show that Lithuania gravel contaminated with reactive particles having amorphous silicon dioxide reacting with cement in sodium and potassium hydroxide and the resulting alkaline concrete corrosion. It was found that, according to AAR 2 large aggregates include Group II – potentially reactive because of their expansion after 14 days, higher than 0.1%. Article in Lithuanian. Lietuvos karjerų užpildų poveikio betono šarminei korozijai tyrimai Santrauka Užpildų šarminė korozija betone vyksta reaguojant cemente esantiems natrio ir kalio hidroksidams (šarmams) su aktyviu SiO2, esančiu kai kuriuose užpilduose. Vykstant šiai reakcijai betone susidaro didelių vidinių įtempių, kurie sukelia betono deformacijas, pleišėjimą ir suirimą. Reakcija vyksta lėtai, betono irimo požymių atsiranda tik po kelių mėnesių ar metų. Tyrimams buvo naudojami dviejų skirtingų karjerų užpildai. Atlikus tyrimus nustatyta, kad Lietuvos žvyro karjerai užteršti reaktyviomis dalelėmis, turinčiomis amorfinio silicio dioksido, reaguojančio su cemente esančiais natrio ir kalio šarmais, ir sukeliančiomis betono šarminę koroziją. Nustatyta, kad pagal AAR 2 stambieji užpildai priskiriami II grupei – galimai reaktyviems užpildams, nes jų plėtra po 14 parų viršija 0,1 %. Reikšminiai žodžiai:betono šarminė korozija, užpildai, reaktyvumas, šarmai, higroskopinis gelis, plėtra.
Lithuanian quarry aggregates concrete effects of alkaline corrosion tests
Aggregate alkaline corrosion of cement in concrete is going to respond in sodium and potassium hydroxide (lye) with active SiO2 found in some aggregates. During this reaction, the concrete has resulted in significant internal stresses which cause deformation of the concrete, cracking and disintegration. The reaction is slow and concrete signs of decomposition appear only after a few months or years. The study used two different aggregates quarries. Studies show that Lithuania gravel contaminated with reactive particles having amorphous silicon dioxide reacting with cement in sodium and potassium hydroxide and the resulting alkaline concrete corrosion. It was found that, according to AAR 2 large aggregates include Group II – potentially reactive because of their expansion after 14 days, higher than 0.1%. Article in Lithuanian. Lietuvos karjerų užpildų poveikio betono šarminei korozijai tyrimai Santrauka Užpildų šarminė korozija betone vyksta reaguojant cemente esantiems natrio ir kalio hidroksidams (šarmams) su aktyviu SiO2, esančiu kai kuriuose užpilduose. Vykstant šiai reakcijai betone susidaro didelių vidinių įtempių, kurie sukelia betono deformacijas, pleišėjimą ir suirimą. Reakcija vyksta lėtai, betono irimo požymių atsiranda tik po kelių mėnesių ar metų. Tyrimams buvo naudojami dviejų skirtingų karjerų užpildai. Atlikus tyrimus nustatyta, kad Lietuvos žvyro karjerai užteršti reaktyviomis dalelėmis, turinčiomis amorfinio silicio dioksido, reaguojančio su cemente esančiais natrio ir kalio šarmais, ir sukeliančiomis betono šarminę koroziją. Nustatyta, kad pagal AAR 2 stambieji užpildai priskiriami II grupei – galimai reaktyviems užpildams, nes jų plėtra po 14 parų viršija 0,1 %. Reikšminiai žodžiai:betono šarminė korozija, užpildai, reaktyvumas, šarmai, higroskopinis gelis, plėtra.
Lithuanian quarry aggregates concrete effects of alkaline corrosion tests
Rutkauskas, Aurimas (author) / Girskas, Giedrius (author)
2016-02-02
doi:10.3846/mla.2015.848
Mokslas – Lietuvos ateitis / Science – Future of Lithuania; Vol 7 No 5 (2015): Civil and transport engineering, aviation technologies / Statyba, transportas, aviacinės technologijos; 551-556 ; 2029-2252 ; 2029-2341
Article (Journal)
Electronic Resource
English
DDC:
690
Identification of Reactivity Level in Aggregates from Lithuanian Gravel Quarry
| DOAJ | 2017
Pit and quarry combine to produce aggregates for concrete road
Engineering Index Backfile | 1929
Strength of Concrete with Ceramic Waste and Quarry Dust as Aggregates
| Tema Archive | 2013
High-strength rice husk ash concrete incorporating quarry dust fine aggregates
| British Library Conference Proceedings | 2010