Rheology characterization of 3D printing mortars with nanoclays and basalt fibers
3D printing has become one of the most innovative technologies for cement-based systems (CBS). However, recent studies have shown some issues related to printability and buildability (water drainage, plugs on extruder die, spreading of first layer, etc). To achieve a proper rheology control of CBS, it is essential to adapt the material fresh state properties (initial shear yield stress and structural build-up). In this study, a reference cement-based mortar with fly ash (25%), a 1:1.5 binder to sand ratio and a 0.38 water to binder ratio was used. A polycarboxilate ether-based superplasticizer was added until a consistency of around 1 kPa, measured with the cone-penetration test, was reached. Then, small amounts of several types of nanoclays (NC) in powder and slurry form (sepiolite, attapulgite and bentonite) and natural fibers were added to modify mortar rheological properties. The aim of the study was to characterize the rheological properties of 3D printing mortar samples with NC and basalt fibers (BF) to understand printability and buildability of this material. Cone-penetration test, flow table test and slump test were used to characterize 3D printing capacities. The cone-penetration test was performed in stirred and left at rest samples to assess shear yield stress before and after material deposition. Nanoclays showed a remarkable capacity to retain water and avoid drainage during extrusion but also to increase fresh state strength of material over time. Besides, they increased shear yield stress over time when left at rest. On the contrary, samples stirred over time did not show any increase of shear yield stress, especially samples with slurry nanoclays. Natural fibers also reduced drainage and enhance printability control regarding to reference mortar. BF also enhanced a performance on stirred sample but showed slightly changes on structural build-up at rest, mainly governed by NC effect. ; Agencia Estatal de Investigación ; Ministerio de Ciencia e Innovación ; Comisión Europea ; Universidad de Alcalá
Rheology characterization of 3D printing mortars with nanoclays and basalt fibers
3D printing has become one of the most innovative technologies for cement-based systems (CBS). However, recent studies have shown some issues related to printability and buildability (water drainage, plugs on extruder die, spreading of first layer, etc). To achieve a proper rheology control of CBS, it is essential to adapt the material fresh state properties (initial shear yield stress and structural build-up). In this study, a reference cement-based mortar with fly ash (25%), a 1:1.5 binder to sand ratio and a 0.38 water to binder ratio was used. A polycarboxilate ether-based superplasticizer was added until a consistency of around 1 kPa, measured with the cone-penetration test, was reached. Then, small amounts of several types of nanoclays (NC) in powder and slurry form (sepiolite, attapulgite and bentonite) and natural fibers were added to modify mortar rheological properties. The aim of the study was to characterize the rheological properties of 3D printing mortar samples with NC and basalt fibers (BF) to understand printability and buildability of this material. Cone-penetration test, flow table test and slump test were used to characterize 3D printing capacities. The cone-penetration test was performed in stirred and left at rest samples to assess shear yield stress before and after material deposition. Nanoclays showed a remarkable capacity to retain water and avoid drainage during extrusion but also to increase fresh state strength of material over time. Besides, they increased shear yield stress over time when left at rest. On the contrary, samples stirred over time did not show any increase of shear yield stress, especially samples with slurry nanoclays. Natural fibers also reduced drainage and enhance printability control regarding to reference mortar. BF also enhanced a performance on stirred sample but showed slightly changes on structural build-up at rest, mainly governed by NC effect. ; Agencia Estatal de Investigación ; Ministerio de Ciencia e Innovación ; Comisión Europea ; Universidad de Alcalá
Rheology characterization of 3D printing mortars with nanoclays and basalt fibers
Varela Recio, Hugo (author) / Barluenga Badiola, Gonzalo (author) / Sonebi , Mohammed (author) / Universidad de Alcalá. Departamento de Arquitectura
2023-07-22
Materials Today: Proceedings
Article (Journal)
Electronic Resource
English
DDC:
624
Effects of Nanoclays on SCC Paste Rheology
| Springer Verlag | 2019
Influence of nanoclays on flowability and rheology of SCC pastes
| Elsevier | 2020