Production and Utilization of Retarder from Hardwood Sawdust
In this study, production of retarding admixture ASTM C494 Type B from hardwood sawdust and utilization on concrete by using various dosage of admixture was studied. In production of retarder as a local product lignosulphonates based retarding admixture was produced to investigate differences of test results by using admixtures. In this project, selected raw material was Pyin Ka do sawdust and sodium sulphite Na2SO3 was used as a cooking aid chemical liquor by heating at 110°C based on pulp and paper sulphite process. The mechanisms of action of lignosulphonate admixture in cement water systems are prescribed by five different types interaction between retarder and cement grains i Reduction in surface tension of water ii Adsorption iii Electrical repulsion iv Dispersion and v Deflocculation. These reactions cause delaying in setting time.In utilization of retarder on concrete, setting time of hydraulic cement paste, compressive strength of mortar and concrete were considered by using produced admixture dosage of 0.5 , 1 , 1.5 by weight of cement. The setting time testing of cement paste was made by using vicat needle penetration test, and compressive strength was tested with standard cubes. The test results of produced admixture were compared with ASTM C494 1993 . Compressive strength of mortar was tested with 3 inches cube and that of concrete was tested by 6 inches standard cube. For comparison of cost and results of produced admixture, commercial admixture 0.5 by weight of cement was tested. Nay Myo Kyaw Thu | Swe Swe Khaing "Production and Utilization of Retarder from Hardwood Sawdust" Published in International Journal of Trend in Scientific Research and Development (ijtsrd), ISSN: 2456-6470, Volume-3 | Issue-5 , August 2019, URL: https://www.ijtsrd.com/papers/ijtsrd27911.pdf
Production and Utilization of Retarder from Hardwood Sawdust
In this study, production of retarding admixture ASTM C494 Type B from hardwood sawdust and utilization on concrete by using various dosage of admixture was studied. In production of retarder as a local product lignosulphonates based retarding admixture was produced to investigate differences of test results by using admixtures. In this project, selected raw material was Pyin Ka do sawdust and sodium sulphite Na2SO3 was used as a cooking aid chemical liquor by heating at 110°C based on pulp and paper sulphite process. The mechanisms of action of lignosulphonate admixture in cement water systems are prescribed by five different types interaction between retarder and cement grains i Reduction in surface tension of water ii Adsorption iii Electrical repulsion iv Dispersion and v Deflocculation. These reactions cause delaying in setting time.In utilization of retarder on concrete, setting time of hydraulic cement paste, compressive strength of mortar and concrete were considered by using produced admixture dosage of 0.5 , 1 , 1.5 by weight of cement. The setting time testing of cement paste was made by using vicat needle penetration test, and compressive strength was tested with standard cubes. The test results of produced admixture were compared with ASTM C494 1993 . Compressive strength of mortar was tested with 3 inches cube and that of concrete was tested by 6 inches standard cube. For comparison of cost and results of produced admixture, commercial admixture 0.5 by weight of cement was tested. Nay Myo Kyaw Thu | Swe Swe Khaing "Production and Utilization of Retarder from Hardwood Sawdust" Published in International Journal of Trend in Scientific Research and Development (ijtsrd), ISSN: 2456-6470, Volume-3 | Issue-5 , August 2019, URL: https://www.ijtsrd.com/papers/ijtsrd27911.pdf
Production and Utilization of Retarder from Hardwood Sawdust
Nay Myo Kyaw Thu (author) / Swe Swe Khaing (author)
2019-12-23
oai:zenodo.org:3591735
International Journal of Trend in Scientific Research and Development 3(5) 1971-1978
Article (Journal)
Electronic Resource
English
DDC:
690
Modified hardwood sawdust as adsorbent of heavy metal ions from water
| British Library Online Contents | 2006
Utilization of borogypsum as set retarder in Portland cement production
| Online Contents | 2002
Utilization of borogypsum as set retarder in Portland cement production
| Tema Archive | 2002
Utilization of borogypsum as set retarder in Portland cement production
| British Library Online Contents | 2002