INFLUENSE OF HIGH TEMPERATURES ON CRACK RESISTANSE CONCRETE STRUCTURE ; ВПЛИВ ВИСОКИХ ТЕМПЕРАТУР НА ТРІЩИНОСТІЙКІСТЬ БЕТОНІВ
The issues connected with crack resistanse and brittle failure of concrete under the influense of raised and high temperatures are investigated. Crack resistanse is considered from the perspective of the concrete brittle failure criterion that connects stress intensity factors during the development of normal bond-failure cracks K1C and cracks that appears during transverse shift KilC with structural changes in concrete caused by temperature. Predicting stress intensity factors and concrete physical characteristics with the account of the temperatures development along the standard fire curve allows to improve methods of calculation of bearing capacity, crack resistanse and deformability of reinforsed concrete structure using principles of mechanics of a rigid body fracture. ; У статті описана методика оцінки крихкого руйнування бетону при пожежі, мета дослідження, методика визначення коефіцієнтів інтенсивності напружень при нормальному відриві КіС та поперечному зсуві Кис- Дослідження проведені на взірцях двох видів бетону - важкому звичайному та керамзитобетоні і дозволяють виконати рекомендації по нормуванню коефіцієнтів інтенсивності напружень, котрі входять до формули визначення критерію крихкого руйнування бетону (Кю), та критеріїв, що використовуються при розрахунку залізобетонних елементів (Кіс • та Кис) з позицій методів механіки руйнування твердих тіл.
INFLUENSE OF HIGH TEMPERATURES ON CRACK RESISTANSE CONCRETE STRUCTURE ; ВПЛИВ ВИСОКИХ ТЕМПЕРАТУР НА ТРІЩИНОСТІЙКІСТЬ БЕТОНІВ
The issues connected with crack resistanse and brittle failure of concrete under the influense of raised and high temperatures are investigated. Crack resistanse is considered from the perspective of the concrete brittle failure criterion that connects stress intensity factors during the development of normal bond-failure cracks K1C and cracks that appears during transverse shift KilC with structural changes in concrete caused by temperature. Predicting stress intensity factors and concrete physical characteristics with the account of the temperatures development along the standard fire curve allows to improve methods of calculation of bearing capacity, crack resistanse and deformability of reinforsed concrete structure using principles of mechanics of a rigid body fracture. ; У статті описана методика оцінки крихкого руйнування бетону при пожежі, мета дослідження, методика визначення коефіцієнтів інтенсивності напружень при нормальному відриві КіС та поперечному зсуві Кис- Дослідження проведені на взірцях двох видів бетону - важкому звичайному та керамзитобетоні і дозволяють виконати рекомендації по нормуванню коефіцієнтів інтенсивності напружень, котрі входять до формули визначення критерію крихкого руйнування бетону (Кю), та критеріїв, що використовуються при розрахунку залізобетонних елементів (Кіс • та Кис) з позицій методів механіки руйнування твердих тіл.
INFLUENSE OF HIGH TEMPERATURES ON CRACK RESISTANSE CONCRETE STRUCTURE ; ВПЛИВ ВИСОКИХ ТЕМПЕРАТУР НА ТРІЩИНОСТІЙКІСТЬ БЕТОНІВ
Pavliuk, Yu. (author)
2020-02-05
Fire Safety; Том 3 (2003): Пожежна безпека; 13-22 ; Пожежна безпека; Том 3 (2003): Пожежна безпека; 13-22 ; 2708-1087 ; 2078-6662
Article (Journal)
Electronic Resource
English