Internal curing of cement pastes by superabsorbent polymers studied by means of neutron radiography
Autogenous shrinkage is a problem in cementitious materials with a low water-to-binder ratio. When the internal relative humidity decreases due to the ongoing hydration reaction and selfdesiccation, autogenous shrinkage takes place if no external or internal water source is present. This may lead to cracking and eventually cause durability problems in constructions. Ideally, the internal relative humidity should be maintained during hydration of the cement paste. Superabsorbent polymers (SAPs) may be used to mitigate autogenous shrinkage. When self-desiccation occurs, these polymers will release their absorbed additional mixing water due to increasing capillary forces to stimulate internal curing. This release of water towards the cementitious matrix and the effect on the cementitious matrix itself can be studied by means of neutron radiography. In this study, thin samples of cement paste were casted between glass plates and the evolution of the internal water amount was studied as a function of time. In specimens without SAPs and a water-to-binder ratio of 0.30, shrinkage was seen. Furthermore, autogenous shrinkage was reduced in cement pastes when using SAPs and an additional entrained water-to-binder ratio of 0.054. The release of water from smaller SAPs (100 μm dry size) seemed to be more promising compared to bigger SAPs (500 μm) with the same absorption properties. The technique of neutron radiography supports the findings of shrinkage tests where SAPs were already proven to be useful. This opens additional insights towards the application of SAPs in the construction area.
Internal curing of cement pastes by superabsorbent polymers studied by means of neutron radiography
Autogenous shrinkage is a problem in cementitious materials with a low water-to-binder ratio. When the internal relative humidity decreases due to the ongoing hydration reaction and selfdesiccation, autogenous shrinkage takes place if no external or internal water source is present. This may lead to cracking and eventually cause durability problems in constructions. Ideally, the internal relative humidity should be maintained during hydration of the cement paste. Superabsorbent polymers (SAPs) may be used to mitigate autogenous shrinkage. When self-desiccation occurs, these polymers will release their absorbed additional mixing water due to increasing capillary forces to stimulate internal curing. This release of water towards the cementitious matrix and the effect on the cementitious matrix itself can be studied by means of neutron radiography. In this study, thin samples of cement paste were casted between glass plates and the evolution of the internal water amount was studied as a function of time. In specimens without SAPs and a water-to-binder ratio of 0.30, shrinkage was seen. Furthermore, autogenous shrinkage was reduced in cement pastes when using SAPs and an additional entrained water-to-binder ratio of 0.054. The release of water from smaller SAPs (100 μm dry size) seemed to be more promising compared to bigger SAPs (500 μm) with the same absorption properties. The technique of neutron radiography supports the findings of shrinkage tests where SAPs were already proven to be useful. This opens additional insights towards the application of SAPs in the construction area.
Internal curing of cement pastes by superabsorbent polymers studied by means of neutron radiography
Snoeck, Didier (author) / Alderete, Natalia Mariel (author) / Van Belleghem, Bjorn (author) / Van den Heede, Philip (author) / Van Tittelboom, Kim (author) / De Belie, Nele (author) / De Schutter, Geert / De Belie, Nele / Janssens, Arnold / Van Den Bossche, Nathan
2017-01-01
XIV DBMC 2017 Conference ; ISBN: 978-2-35158-159-9
Conference paper
Electronic Resource
English
DDC:
690
Autogenous strain of cement pastes with superabsorbent polymers
| British Library Conference Proceedings | 2006
Compressive strength of cement pastes and mortars with superabsorbent polymers
| British Library Conference Proceedings | 2006
Early-state water migration characteristics of superabsorbent polymers in cement pastes
| British Library Online Contents | 2019
Suitability of polyacrylamide superabsorbent polymers as the internal curing agent of well cement
| Online Contents | 2016