Water Penetration of Concrete made with Coarse Aggregates from Demolishing Waste
The results of laboratory investigations on water penetration in concrete made with coarse aggregates from demolishing waste are presented in this paper. Seven batches of standard size concrete cubes were cast with recycled aggregates from demolished concrete replacing coarse aggregates in percentages from 0% to 60%. The compressive strength of the samples was evaluated by non-destructive testing with the use of the Schimidz hammer. It was found that the strength reduces with an increase in recycled aggregate percentage. The maximum loss of strength due to the induction of recycled aggregates was 32% in the batch with 60%recycled aggregates. All samples were subject to constant water pressure of 5 bars for 72 hours. From the obtained results it was shown that the water penetration depth increases with increase in recycled aggregates rate. With 10% and 20% replacement the samples allowed less water to penetrate than conventional concrete samples, but 76% more penetration depth was recorded in samples with 60% replacement. Strength and water penetration results from dosages up to 20% show that the durability of the produced concrete allows it to be used in structural members with consideration of strength reduction in the design process. However, more water penetration with higher dosages of recycled aggregates needs proper care in design and usage of the concrete particularly for locations where concrete is exposed to water pressure.
Water Penetration of Concrete made with Coarse Aggregates from Demolishing Waste
The results of laboratory investigations on water penetration in concrete made with coarse aggregates from demolishing waste are presented in this paper. Seven batches of standard size concrete cubes were cast with recycled aggregates from demolished concrete replacing coarse aggregates in percentages from 0% to 60%. The compressive strength of the samples was evaluated by non-destructive testing with the use of the Schimidz hammer. It was found that the strength reduces with an increase in recycled aggregate percentage. The maximum loss of strength due to the induction of recycled aggregates was 32% in the batch with 60%recycled aggregates. All samples were subject to constant water pressure of 5 bars for 72 hours. From the obtained results it was shown that the water penetration depth increases with increase in recycled aggregates rate. With 10% and 20% replacement the samples allowed less water to penetrate than conventional concrete samples, but 76% more penetration depth was recorded in samples with 60% replacement. Strength and water penetration results from dosages up to 20% show that the durability of the produced concrete allows it to be used in structural members with consideration of strength reduction in the design process. However, more water penetration with higher dosages of recycled aggregates needs proper care in design and usage of the concrete particularly for locations where concrete is exposed to water pressure.
Water Penetration of Concrete made with Coarse Aggregates from Demolishing Waste
Koondhar, M. F. (author) / Memon, B. A. (author) / Oad, M. (author) / Chandio, F. A. (author) / Chandio, S. A. (author)
2020-12-20
oai:zenodo.org:4421719
Engineering, Technology & Applied Science Research 10(6) 6445-6449
Article (Journal)
Electronic Resource
English
DDC:
690
REINFORCED CONCRETE STRUCTURE DEMOLISHING SYSTEM AND DEMOLISHING METHOD
| European Patent Office | 2023
Demolishing concrete bridges with explosives
Engineering Index Backfile | 1936
Cracking susceptibility of concrete made with coarse recycled concrete aggregates
| Online Contents | 2016
Cracking susceptibility of concrete made with coarse recycled concrete aggregates
| British Library Online Contents | 2016
Cracking susceptibility of concrete made with coarse recycled concrete aggregates
| Online Contents | 2016