Evaluation of the Loss of Uniaxial Compressive Strength of Sandstones Due to Moisture
The reduction in uniaxial compressive strength (UCS) was investigated for sandstones under various moisture levels. Thirty-four UK Darney sandstone samples were tested under six different moisture conditions. The time-dependent moisture gain and loss were also evaluated. For 77 sandstones identified in the literature, the loss of UCS between oven-dry and saturated conditions was up to 45%, with an average of 20%. For Darney stone, the average loss of UCS was around 20%, with UCS around 72 N/mm2 when oven-dry and 58 N/mm2 when fully saturated. During saturation, significant loss of UCS occurred soon after exposure to water with 80% of UCS being lost within the first 2.5–6 hours. For Darney stone 50% of UCS was lost at air-dry conditions. Results from the 78 sandstone types were compared with the equivalent compressive strength defined by BS EN 772–1:2011 for oven-dry, air-dry, and saturated conditions. The estimated values by BS EN 772–1:2011 for dry and saturated UCS agreed well with the available test data and indicated a lower-bound solution. For immersed conditions, BS EN 772–1:2011, however, overestimates the reduction in UCS for a large number of samples and provides an average, instead of a lower-bound solution.
Evaluation of the Loss of Uniaxial Compressive Strength of Sandstones Due to Moisture
The reduction in uniaxial compressive strength (UCS) was investigated for sandstones under various moisture levels. Thirty-four UK Darney sandstone samples were tested under six different moisture conditions. The time-dependent moisture gain and loss were also evaluated. For 77 sandstones identified in the literature, the loss of UCS between oven-dry and saturated conditions was up to 45%, with an average of 20%. For Darney stone, the average loss of UCS was around 20%, with UCS around 72 N/mm2 when oven-dry and 58 N/mm2 when fully saturated. During saturation, significant loss of UCS occurred soon after exposure to water with 80% of UCS being lost within the first 2.5–6 hours. For Darney stone 50% of UCS was lost at air-dry conditions. Results from the 78 sandstone types were compared with the equivalent compressive strength defined by BS EN 772–1:2011 for oven-dry, air-dry, and saturated conditions. The estimated values by BS EN 772–1:2011 for dry and saturated UCS agreed well with the available test data and indicated a lower-bound solution. For immersed conditions, BS EN 772–1:2011, however, overestimates the reduction in UCS for a large number of samples and provides an average, instead of a lower-bound solution.
Evaluation of the Loss of Uniaxial Compressive Strength of Sandstones Due to Moisture
Tomor, Adrienn K (author) / Nichols, John M (author) / Orbán, Zoltán (author)
2023-03-17
International Journal of Architectural Heritage (2023) (In press).
Article (Journal)
Electronic Resource
English
DDC:
690
Evaluation of the Loss of Uniaxial Compressive Strength of Sandstones Due to Moisture
| Taylor & Francis Verlag | 2024
Prediction of uniaxial compressive strength of sandstones using petrography-based models
| Online Contents | 2008
Prediction of uniaxial compressive strength of sandstones using petrography-based models
| Tema Archive | 2008
Prediction of uniaxial compressive strength of sandstones using petrography-based models
| British Library Online Contents | 2008