Effect of microfibrillar cellulose on concrete equivalent mortar fresh and hardened properties ; Inverkan av mikrofibrillär cellulosa på egenskaperna hos betongekvivelent bruk i dess färska och hårdnade tillstånd
A pilot project in 2010, conducted at CBI, showed the capacity for pulp, micro fibrilars from the forest industry to act as Viscosity Modifying Agent (VMA) in concrete. This project was, however, too limited to find answers for optimal use of this kind of material. The forest industry company Stora Enso wants to find out if their pulp can be used in concrete in order to somehow improve its properties. Two micro fibrilar suspensions have been tested. The tested fibrils are in two sizes, the finer material named MFC1 has undergone more homogenization than the course material named MFC2. The fibrils have been evaluated in regard to how the fibrils react with mortars in both its fresh and hardened state. Tests have been conducted on the use of concrete equivalent mortars with a maximum aggregates size of 4 mm. Two water-cement-ratios have been used in the tests, 0.45 and 0.60. Three different fibril dosages have been tested, 1, 2 and 3 kg/m³. The results of these trials of cellulose fibrils has been evaluated in respect of rheology, compressive strength, flexural strength, cracking, shrinkage, water capillary porosity, anti-wash out resistance (underwater concrete) and as a possible surface coverage. The results from the trials, conducted in this report, show that an increased dosage of fibrils leads to an increased plastic viscosity. The fibrils appear to have no effect on the flexural- and compressive strength, and no effect on the shrinkage of the test specimens. According to our results it is not advisable to use the fibrils for the purpose of acting as an agent for anti-washout resistance, or as a surface coverage. The work have been performed at Swedish Cement and Concrete Research Institute, CBI, in Stockholm in the spring of 2011. CBI is an institution whose mission is to create, apply and disseminate knowledge in the concrete and rock area. ; Ett tidigare pilotprojekt har under 2010 utförts på CBI, och där undersöktes möjligheten för cellulosafibrer från skogsindustrin att fungera som Viscosity Modifying ...
Effect of microfibrillar cellulose on concrete equivalent mortar fresh and hardened properties ; Inverkan av mikrofibrillär cellulosa på egenskaperna hos betongekvivelent bruk i dess färska och hårdnade tillstånd
A pilot project in 2010, conducted at CBI, showed the capacity for pulp, micro fibrilars from the forest industry to act as Viscosity Modifying Agent (VMA) in concrete. This project was, however, too limited to find answers for optimal use of this kind of material. The forest industry company Stora Enso wants to find out if their pulp can be used in concrete in order to somehow improve its properties. Two micro fibrilar suspensions have been tested. The tested fibrils are in two sizes, the finer material named MFC1 has undergone more homogenization than the course material named MFC2. The fibrils have been evaluated in regard to how the fibrils react with mortars in both its fresh and hardened state. Tests have been conducted on the use of concrete equivalent mortars with a maximum aggregates size of 4 mm. Two water-cement-ratios have been used in the tests, 0.45 and 0.60. Three different fibril dosages have been tested, 1, 2 and 3 kg/m³. The results of these trials of cellulose fibrils has been evaluated in respect of rheology, compressive strength, flexural strength, cracking, shrinkage, water capillary porosity, anti-wash out resistance (underwater concrete) and as a possible surface coverage. The results from the trials, conducted in this report, show that an increased dosage of fibrils leads to an increased plastic viscosity. The fibrils appear to have no effect on the flexural- and compressive strength, and no effect on the shrinkage of the test specimens. According to our results it is not advisable to use the fibrils for the purpose of acting as an agent for anti-washout resistance, or as a surface coverage. The work have been performed at Swedish Cement and Concrete Research Institute, CBI, in Stockholm in the spring of 2011. CBI is an institution whose mission is to create, apply and disseminate knowledge in the concrete and rock area. ; Ett tidigare pilotprojekt har under 2010 utförts på CBI, och där undersöktes möjligheten för cellulosafibrer från skogsindustrin att fungera som Viscosity Modifying ...
Effect of microfibrillar cellulose on concrete equivalent mortar fresh and hardened properties ; Inverkan av mikrofibrillär cellulosa på egenskaperna hos betongekvivelent bruk i dess färska och hårdnade tillstånd
Nilsson, Jonas (author) / Sargenius, Peter (author)
2011-01-01
Theses
Electronic Resource
English
DDC:
690
A review on properties of fresh and hardened geopolymer mortar
| British Library Online Contents | 2018
Properties of fresh and hardened concrete
| British Library Online Contents | 2011
Properties of fresh and hardened concrete
| Online Contents | 2011
Dynamic properties of hardened paste, mortar and concrete
| Springer Verlag | 1971