Synthesis of fluorinated polymers in supercritical carbon dioxide (scCO₂) ; Synthese von Fluorpolymeren in überkritischem Kohlendioxid (scCO₂)
For the first time stabilizer-free vinylidene fluoride (VDF) polymerizations were carried out in homogeneous phase with supercritical CO₂. Polymerizations were carried out at 140°C, 1500 bar and were initiated with di-tert-butyl peroxide (DTBP). In-line FT-NIR (Fourier Transform- Near Infrared) spectroscopy showed that complete monomer conversion may be obtained. Molecular weights were determined via size-exclusion chromatography (SEC) and polymer end group analysis by 1H-NMR spectroscopy. The number average molecular weights were below 104 g∙mol−1 and polydispersities ranged from 3.1 to 5.7 depending on DTBP and VDF concentration. To allow for isothermal reactions high CO₂ contents ranging from 61 to 83 wt.% were used. The high-temperature, high-pressure conditions were required for homogeneous phase polymerization. These conditions did not alter the amount of defects in VDF chaining. Scanning electron microscopy (SEM) indicated that regular stack-type particles were obtained upon expansion of the homogeneous polymerization mixture. To reduce the required amount of initiator, further VDF polymerizations using chain transfer agents (CTAs) to control molecular weights were carried out in homogeneous phase with supercritical carbon dioxide (scCO₂) at 120 °C and 1500 bar. Using perfluorinated hexyl iodide as CTA, polymers of low polydispersity ranging from 1.5 to 1.2 at the highest iodide concentration of 0.25 mol·L-1 were obtained. Electrospray ionization- mass spectroscopy (ESI-MS) indicates the absence of initiator derived end groups, supporting livingness of the system. The “livingness” is based on the labile C-I bond. However, due to the weakness of the C-I bond perfluorinated hexyl iodide also contributes to initiation. To allow for kinetic analyses of VDF polymerizations the CTA should not contribute to initiation. Therefore, additional CTAs were applied: BrCCl3, C6F13Br and C6F13H. It was found that C6F13H does not contribute to initiation. At 120°C and 1500 bar kp/kt0.5~ 0.64 (L·mol−1·s−1)0.5 was derived. ...
Synthesis of fluorinated polymers in supercritical carbon dioxide (scCO₂) ; Synthese von Fluorpolymeren in überkritischem Kohlendioxid (scCO₂)
For the first time stabilizer-free vinylidene fluoride (VDF) polymerizations were carried out in homogeneous phase with supercritical CO₂. Polymerizations were carried out at 140°C, 1500 bar and were initiated with di-tert-butyl peroxide (DTBP). In-line FT-NIR (Fourier Transform- Near Infrared) spectroscopy showed that complete monomer conversion may be obtained. Molecular weights were determined via size-exclusion chromatography (SEC) and polymer end group analysis by 1H-NMR spectroscopy. The number average molecular weights were below 104 g∙mol−1 and polydispersities ranged from 3.1 to 5.7 depending on DTBP and VDF concentration. To allow for isothermal reactions high CO₂ contents ranging from 61 to 83 wt.% were used. The high-temperature, high-pressure conditions were required for homogeneous phase polymerization. These conditions did not alter the amount of defects in VDF chaining. Scanning electron microscopy (SEM) indicated that regular stack-type particles were obtained upon expansion of the homogeneous polymerization mixture. To reduce the required amount of initiator, further VDF polymerizations using chain transfer agents (CTAs) to control molecular weights were carried out in homogeneous phase with supercritical carbon dioxide (scCO₂) at 120 °C and 1500 bar. Using perfluorinated hexyl iodide as CTA, polymers of low polydispersity ranging from 1.5 to 1.2 at the highest iodide concentration of 0.25 mol·L-1 were obtained. Electrospray ionization- mass spectroscopy (ESI-MS) indicates the absence of initiator derived end groups, supporting livingness of the system. The “livingness” is based on the labile C-I bond. However, due to the weakness of the C-I bond perfluorinated hexyl iodide also contributes to initiation. To allow for kinetic analyses of VDF polymerizations the CTA should not contribute to initiation. Therefore, additional CTAs were applied: BrCCl3, C6F13Br and C6F13H. It was found that C6F13H does not contribute to initiation. At 120°C and 1500 bar kp/kt0.5~ 0.64 (L·mol−1·s−1)0.5 was derived. ...
Synthesis of fluorinated polymers in supercritical carbon dioxide (scCO₂) ; Synthese von Fluorpolymeren in überkritischem Kohlendioxid (scCO₂)
Imran ul-haq, Muhammad (author)
2008-08-18
Theses
Electronic Resource
English
Extraktion aus biokatalytischen Reaktionsgemischen mit scCO2
| Wiley | 2009
Reactive Transport of scCO2 within Cement Paste
| ASCE | 2013
Depolymerisationen in überkritischem Kohlendioxid
| Wiley | 2003