KUALITAS PAPAN KOMPOSIT DARI LIMBAH FINIR KAYU LAPIS BERDASARKAN UKURAN PARTIKEL DAN WAKTU PENGEMPAAN DENGAN MENGGUNAKAN PEREKAT LIMBAH PLASTIK POLIPROPILENA
This study aims to analyze the quality of composite boards from plywood veneers waste and polypropylene plastic waste adhesives base on particle sizes, pressing times, and both of interaction towards physical and mechanical properties also to obtain the particle sizes and pressing time properly with the result that produce the qualified standard boards of JIS A 5908-2003. This research carried out at the wood workshop, laboratory of technology and processing of woods (the faculty of forestry, university of Tanjungpura), and the laboratory of PT. Duta Pertiwi Nusantara. The materials used in this study were plywood veneers waste and polypropylene plastic by 50% : 50% comparison. The research method was utilized the completely randomized factorial design by two treatment factors. Factor A was particle sizes that consisting of 6 mesh, 8 mesh, and 10 mesh. Factor B was pressing time that consisting of 10 minutes, 15 minute, and 20 minutes. Composite boards were created by 30 x 30 x 1 size in centimetres by means the density target was 0,7 gr/cm3. The pressing was done by hot press in 180oC temperature and composite boards conditioning for 14 days. The results of this study showed that the density, water absorption, thickness, Modulus of Repture (MOR), internal bonding, holding strength of screws in the composite boards have been qualified the standard of JIS A 5908-2003. While, the water contents and Modulus of Elasticity (MOE) testing were not qualified the standard of JIS 5908-2003. The treatment that produce the optimum composite boards which quality JIS A 5908-2003 standard was on the 8 mesh particle size treatment by means of 15 minutes pressing time.Keywords: Composite Board, Particle Size, Polypropylene Plastics, Pressing Time, Veneers Waste.
KUALITAS PAPAN KOMPOSIT DARI LIMBAH FINIR KAYU LAPIS BERDASARKAN UKURAN PARTIKEL DAN WAKTU PENGEMPAAN DENGAN MENGGUNAKAN PEREKAT LIMBAH PLASTIK POLIPROPILENA
This study aims to analyze the quality of composite boards from plywood veneers waste and polypropylene plastic waste adhesives base on particle sizes, pressing times, and both of interaction towards physical and mechanical properties also to obtain the particle sizes and pressing time properly with the result that produce the qualified standard boards of JIS A 5908-2003. This research carried out at the wood workshop, laboratory of technology and processing of woods (the faculty of forestry, university of Tanjungpura), and the laboratory of PT. Duta Pertiwi Nusantara. The materials used in this study were plywood veneers waste and polypropylene plastic by 50% : 50% comparison. The research method was utilized the completely randomized factorial design by two treatment factors. Factor A was particle sizes that consisting of 6 mesh, 8 mesh, and 10 mesh. Factor B was pressing time that consisting of 10 minutes, 15 minute, and 20 minutes. Composite boards were created by 30 x 30 x 1 size in centimetres by means the density target was 0,7 gr/cm3. The pressing was done by hot press in 180oC temperature and composite boards conditioning for 14 days. The results of this study showed that the density, water absorption, thickness, Modulus of Repture (MOR), internal bonding, holding strength of screws in the composite boards have been qualified the standard of JIS A 5908-2003. While, the water contents and Modulus of Elasticity (MOE) testing were not qualified the standard of JIS 5908-2003. The treatment that produce the optimum composite boards which quality JIS A 5908-2003 standard was on the 8 mesh particle size treatment by means of 15 minutes pressing time.Keywords: Composite Board, Particle Size, Polypropylene Plastics, Pressing Time, Veneers Waste.
KUALITAS PAPAN KOMPOSIT DARI LIMBAH FINIR KAYU LAPIS BERDASARKAN UKURAN PARTIKEL DAN WAKTU PENGEMPAAN DENGAN MENGGUNAKAN PEREKAT LIMBAH PLASTIK POLIPROPILENA
Rodriquez, Alfonsus (author) / Yani, Ahmad (author) / Yusro, Fathul (author)
2019-08-14
doi:10.26418/jhl.v7i2.34757
JURNAL HUTAN LESTARI; Vol 7, No 2 (2019): JURNAL HUTAN LESTARI ; 2776-1754 ; 2338-3127 ; 10.26418/jhl.v7i2
Article (Journal)
Electronic Resource
English
DDC:
690
Pengembangan Perekat Likuid dan Papan Partikel dari Limbah Tandan Kosong Sawit
| BASE | 2014
PAPAN PARTIKEL DARI SERBUK KAYU DAN LIMBAH PENYULINGAN KULIT KAYU GEMOR (Alseodaphne spp.)
| BASE | 2013