FIRE RESISTANT ABILITY OF FILLED SILICONE ORGANIC COATINGS FOR CONCRETE ; ВОГНЕЗАХИСНА ЗДАТНІСТЬ НАПОВНЕНИХ СИЛІЦІЙОРГАНІЧНИХ ПОКРИТТІВ ДЛЯ БЕТОНУ
The issue of fire resistant efficiency of filled silicone organic coatings for concrete was considered, which is based on the formation of expanded thermo-insulating layer on surface of the concrete structure at temperature of 473-773 K. Due to low thermal conductivity the porous thermoinsulating coating layer prevents rapid heating of protected building structure. Fire resistant ability of coatings for concrete was researched according to standardized methodology, which is based on determining linear expansion ratio of fire resistant material. The composition of fire resistant coatings, which are characterized by the highest linear expansion ratios and the lowest thermal conductivity characteristics, was determined. ; Розглянуто питання вогнезахисної здатності наповнених силіційорганічних покриттів для бетону, яка ґрунтується на утворенні спученого термоізоляційного шару на поверхні бетонної конструкції за температури 473-773 К. Завдяки низькій теплопровідності пористий термоізоляційний шар покриття запобігає швидкому прогріву захищуваної будівельної конструкції. Досліджено вогнезахисну здатність покриття для бетону за стандартизованою методикою, яка базується на визначенні лінійного коефіцієнта спучення матеріалу покриття. Встановлено склади вогнезахисних покриттів, які характеризуються найвищими лінійними коефіцієнтами спучення та найнижчими характеристиками коефіцієнтів теплопровідності.
FIRE RESISTANT ABILITY OF FILLED SILICONE ORGANIC COATINGS FOR CONCRETE ; ВОГНЕЗАХИСНА ЗДАТНІСТЬ НАПОВНЕНИХ СИЛІЦІЙОРГАНІЧНИХ ПОКРИТТІВ ДЛЯ БЕТОНУ
The issue of fire resistant efficiency of filled silicone organic coatings for concrete was considered, which is based on the formation of expanded thermo-insulating layer on surface of the concrete structure at temperature of 473-773 K. Due to low thermal conductivity the porous thermoinsulating coating layer prevents rapid heating of protected building structure. Fire resistant ability of coatings for concrete was researched according to standardized methodology, which is based on determining linear expansion ratio of fire resistant material. The composition of fire resistant coatings, which are characterized by the highest linear expansion ratios and the lowest thermal conductivity characteristics, was determined. ; Розглянуто питання вогнезахисної здатності наповнених силіційорганічних покриттів для бетону, яка ґрунтується на утворенні спученого термоізоляційного шару на поверхні бетонної конструкції за температури 473-773 К. Завдяки низькій теплопровідності пористий термоізоляційний шар покриття запобігає швидкому прогріву захищуваної будівельної конструкції. Досліджено вогнезахисну здатність покриття для бетону за стандартизованою методикою, яка базується на визначенні лінійного коефіцієнта спучення матеріалу покриття. Встановлено склади вогнезахисних покриттів, які характеризуються найвищими лінійними коефіцієнтами спучення та найнижчими характеристиками коефіцієнтів теплопровідності.
FIRE RESISTANT ABILITY OF FILLED SILICONE ORGANIC COATINGS FOR CONCRETE ; ВОГНЕЗАХИСНА ЗДАТНІСТЬ НАПОВНЕНИХ СИЛІЦІЙОРГАНІЧНИХ ПОКРИТТІВ ДЛЯ БЕТОНУ
Yakovchuk, R. S. (author) / Parkhomenko, R. S. (author) / Hyvlyud, М. M. (author) / Stashkо, N. Р. (author)
2018-10-22
Fire Safety; Том 22 (2013): Пожежна безпека; 222-226 ; Пожежна безпека; Том 22 (2013): Пожежна безпека; 222-226 ; 2708-1087 ; 2078-6662
Article (Journal)
Electronic Resource
English
DDC:
624
Fire Resistance of Concrete-Filled, Fire-Resistant Steel-Tube Columns
| British Library Online Contents | 1994