Flexural Behavior of Graphene Nanoplatelets Reinforced Cross-Ply Eglass/ epoxy Laminated Composite Materials ; Grafen Nanopul Takviyeli Çapraz Katlı E-cam lifi/Epoksi Tabakalı Kompozit Malzemelerin Eğilme Davranışı
In this study, the effect of graphene nanoplatelets reinforcement on the flexural strength of Eglass/ epoxy laminated composite material was investigated experimentally. [0?/90?]3S oriented composite materials with and without graphene nanoplatelets reinforcement were manufactured by using hand lay-up and vacuum bagging method. Graphene nanoplatelets at three different ratios (0.25, 0.5 and 1 wt.%) were added to the epoxy. The produced plates were cut with a water jet cutting machine to obtain three-point bending specimens. Then, three-point bending tests were performed according to the ASTM D790 standard. The span between the centers of support cylinders/composite specimen thickness ratio (s/t) was selected as 16 in all the tests. Results indicate that the addition of graphene nanoplatelets to the epoxy matrix increased the flexural strength of the laminated composite material. When the graphene nanoplatelets at ratios of 0.25, 0.5 and 1 wt.% were added to the epoxy matrix, the flexural strengths increased by 4.32%, 12.88% and 7.03% respectively. ; Bu çalışmada grafen nanopul takviyesinin E-cam lifi/epoksi tabakalı kompozit malzemenin esneklik mukavemeti üzerine etkisi deneysel olarak araştırılmıştır. Grafen nanopul takviyeli ve takviyesiz, [0o/90o]3S fiber oryantasyonuna sahip kompozit malzemeler el yatırma ve vakum torbalama yöntemiyle imal edilmiştir. Epoksi içerisine ağırlıkça üç farklı oranda (% 0.25, 0.5 ve 1) grafen nanopul eklenmiştir. Üretimi yapılan plakalar su jeti kesme makinasıyla kesilerek üç nokta eğme test numuneleri elde edilmiştir. Daha sonra ASTM D790 standardına göre üç nokta eğme testleri yapılmıştır. Destek silindirlerinin merkezleri arasındaki mesafe/kompozit numune kalınlığı oranı (s/t) tüm testlerde 16 olarak seçilmiştir. Elde edilen sonuçlara göre epoksi matris içerisine grafen nanopul eklenmesi, tabakalı kompozit malzemenin esneklik mukavemetini artırmıştır. Epoksi matris içerisine ağırlıkça % 0.25, 0.5 ve 1 oranlarında grafen nanopul katıldığında esneklik mukavemetinde sırasıyla % 4.32, 12.88 ve 7.03’lük bir artış olmuştur.
Flexural Behavior of Graphene Nanoplatelets Reinforced Cross-Ply Eglass/ epoxy Laminated Composite Materials ; Grafen Nanopul Takviyeli Çapraz Katlı E-cam lifi/Epoksi Tabakalı Kompozit Malzemelerin Eğilme Davranışı
In this study, the effect of graphene nanoplatelets reinforcement on the flexural strength of Eglass/ epoxy laminated composite material was investigated experimentally. [0?/90?]3S oriented composite materials with and without graphene nanoplatelets reinforcement were manufactured by using hand lay-up and vacuum bagging method. Graphene nanoplatelets at three different ratios (0.25, 0.5 and 1 wt.%) were added to the epoxy. The produced plates were cut with a water jet cutting machine to obtain three-point bending specimens. Then, three-point bending tests were performed according to the ASTM D790 standard. The span between the centers of support cylinders/composite specimen thickness ratio (s/t) was selected as 16 in all the tests. Results indicate that the addition of graphene nanoplatelets to the epoxy matrix increased the flexural strength of the laminated composite material. When the graphene nanoplatelets at ratios of 0.25, 0.5 and 1 wt.% were added to the epoxy matrix, the flexural strengths increased by 4.32%, 12.88% and 7.03% respectively. ; Bu çalışmada grafen nanopul takviyesinin E-cam lifi/epoksi tabakalı kompozit malzemenin esneklik mukavemeti üzerine etkisi deneysel olarak araştırılmıştır. Grafen nanopul takviyeli ve takviyesiz, [0o/90o]3S fiber oryantasyonuna sahip kompozit malzemeler el yatırma ve vakum torbalama yöntemiyle imal edilmiştir. Epoksi içerisine ağırlıkça üç farklı oranda (% 0.25, 0.5 ve 1) grafen nanopul eklenmiştir. Üretimi yapılan plakalar su jeti kesme makinasıyla kesilerek üç nokta eğme test numuneleri elde edilmiştir. Daha sonra ASTM D790 standardına göre üç nokta eğme testleri yapılmıştır. Destek silindirlerinin merkezleri arasındaki mesafe/kompozit numune kalınlığı oranı (s/t) tüm testlerde 16 olarak seçilmiştir. Elde edilen sonuçlara göre epoksi matris içerisine grafen nanopul eklenmesi, tabakalı kompozit malzemenin esneklik mukavemetini artırmıştır. Epoksi matris içerisine ağırlıkça % 0.25, 0.5 ve 1 oranlarında grafen nanopul katıldığında esneklik mukavemetinde sırasıyla % 4.32, 12.88 ve 7.03’lük bir artış olmuştur.
Flexural Behavior of Graphene Nanoplatelets Reinforced Cross-Ply Eglass/ epoxy Laminated Composite Materials ; Grafen Nanopul Takviyeli Çapraz Katlı E-cam lifi/Epoksi Tabakalı Kompozit Malzemelerin Eğilme Davranışı
Sakine Kıratlı (author) / Züleyha Aslan (author) / Sivas Cumhuriyet Üniversitesi
2018-01-01
531
Article (Journal)
Electronic Resource
English
DDC:
690
Fabrication and characterization of laminated SiC composites reinforced with graphene nanoplatelets
| British Library Online Contents | 2016
Flexural Behavior of Composite Concrete–Epoxy–Reinforced Concrete Beams
| Springer Verlag | 2020
In situ processing of epoxy composites reinforced with graphene nanoplatelets
| British Library Online Contents | 2013