Feasibility of Nickel–Aluminum Complex Hydroxides for Recovering Tungsten Ions from Aqueous Media
In this study, the adsorption and/or desorption capacity of tungsten ions using nickel–aluminum complex hydroxides was assessed. Nickel–aluminum complex hydroxides at various molar ratios, such as NA11 were prepared, and the adsorption capacity of tungsten ions was evaluated. Precisely, the effect of temperature, contact time, pH, and coexistence on the adsorption of tungsten ions in the water layer was demonstrated. Among the nickel–aluminum complex hydroxides at various molar ratios, the adsorption capacity onto NA11 was the highest of all adsorbents. The sulfate ions in the interlayer of NA11 was exchanged to tungsten ions, that is, the adsorption mechanism was ion exchange under our experimental conditions. Additionally, to elucidate the adsorption mechanism in detail, the elemental distribution and X-ray photoelectron spectroscopy of the NA11 surface were analyzed. Finally, the results indicated that the tungsten ions adsorbed using NA11 could be desorbed (recovered) from NA11 using sodium hydroxide solution. These results serve as useful information regarding the adsorption and recovery of tungsten ions using nickel–aluminum complex hydroxides from aqueous media.
Feasibility of Nickel–Aluminum Complex Hydroxides for Recovering Tungsten Ions from Aqueous Media
In this study, the adsorption and/or desorption capacity of tungsten ions using nickel–aluminum complex hydroxides was assessed. Nickel–aluminum complex hydroxides at various molar ratios, such as NA11 were prepared, and the adsorption capacity of tungsten ions was evaluated. Precisely, the effect of temperature, contact time, pH, and coexistence on the adsorption of tungsten ions in the water layer was demonstrated. Among the nickel–aluminum complex hydroxides at various molar ratios, the adsorption capacity onto NA11 was the highest of all adsorbents. The sulfate ions in the interlayer of NA11 was exchanged to tungsten ions, that is, the adsorption mechanism was ion exchange under our experimental conditions. Additionally, to elucidate the adsorption mechanism in detail, the elemental distribution and X-ray photoelectron spectroscopy of the NA11 surface were analyzed. Finally, the results indicated that the tungsten ions adsorbed using NA11 could be desorbed (recovered) from NA11 using sodium hydroxide solution. These results serve as useful information regarding the adsorption and recovery of tungsten ions using nickel–aluminum complex hydroxides from aqueous media.
Feasibility of Nickel–Aluminum Complex Hydroxides for Recovering Tungsten Ions from Aqueous Media
Fumihiko Ogata (author) / Saki Kawamoto (author) / Ayako Tabuchi (author) / Megumu Toda (author) / Masashi Otani (author) / Takehiro Nakamura (author) / Naohito Kawasaki (author)
2022
Article (Journal)
Electronic Resource
Unknown
Metadata by DOAJ is licensed under CC BY-SA 1.0
Electrode Properties of Nickel-Aluminum Layered Double Hydroxides in Aqueous Electrolyte Solutions
| British Library Online Contents | 2013
Heteropoly blue-intercalated layered double hydroxides for cationic dye removal from aqueous media
| Online Contents | 2011
Interstratification in the Substituted Nickel Hydroxides
| British Library Online Contents | 1994