Impact testing with controlled energy of multiaxial aramid fabrics with various types of reinforcement
The physical and mechanical properties of the six samples of polyurethane/p-aramid multiaxial fabric forms (Kolon fabrics) were analyzed by high speed impact tester. The samples were impregnated with 10 wt.% poly (vinyl butyral) (PVB)/ethanol solution and modified with γ-aminopropyltriethoxysilane (AMEO silane)/ethanol solution. Unmodified silica (SiO2) nanoparticles, tungsten disulfide (WS2) nanoparticles and multiwalled carbon nanotubes (MWCNT) were used as reinforcement for multiaxial Kolon fabrics. The SiO2/PVB mass fraction was 10 wt.%, while the WS2/PVB and MWCNT/PVB mass fractions were the same - 1 wt.%. The results revealed the increase of the maximal impact force and the total energy absorbed for all the samples compared to the unmodified Kolon fabric sample and the application possibilities of these materials for the antiballistic protection.
Impact testing with controlled energy of multiaxial aramid fabrics with various types of reinforcement
The physical and mechanical properties of the six samples of polyurethane/p-aramid multiaxial fabric forms (Kolon fabrics) were analyzed by high speed impact tester. The samples were impregnated with 10 wt.% poly (vinyl butyral) (PVB)/ethanol solution and modified with γ-aminopropyltriethoxysilane (AMEO silane)/ethanol solution. Unmodified silica (SiO2) nanoparticles, tungsten disulfide (WS2) nanoparticles and multiwalled carbon nanotubes (MWCNT) were used as reinforcement for multiaxial Kolon fabrics. The SiO2/PVB mass fraction was 10 wt.%, while the WS2/PVB and MWCNT/PVB mass fractions were the same - 1 wt.%. The results revealed the increase of the maximal impact force and the total energy absorbed for all the samples compared to the unmodified Kolon fabric sample and the application possibilities of these materials for the antiballistic protection.
Impact testing with controlled energy of multiaxial aramid fabrics with various types of reinforcement
Obradović Vera M. (author) / Stojanović Dušica B. (author) / Radojević Vesna J. (author) / Uskoković Petar S. (author) / Aleksić Radoslav R. (author)
2015
Article (Journal)
Electronic Resource
Unknown
Metadata by DOAJ is licensed under CC BY-SA 1.0
The viscoelastic properties of modified thermoplastic impregnated multiaxial aramid fabrics
| British Library Online Contents | 2012
Multiaxial layer fabrics show their strength
British Library Online Contents | 1997
Tensile Behaviors of Basalt, Carbon, Glass, and Aramid Fabrics under Various Strain Rates
| Online Contents | 2016
Tensile Behaviors of Basalt, Carbon, Glass, and Aramid Fabrics under Various Strain Rates
| Online Contents | 2016
Tensile Behaviors of Basalt, Carbon, Glass, and Aramid Fabrics under Various Strain Rates
| British Library Online Contents | 2016