THE INFLUENCE OF SIZE EFFECT ON THE FRACTURE STRENGTH OF UNIDIRECTIONAL GLASS FIBER REINFORCED POLYPROPYLENE COMPOSITE
In order to explore the influence of the size effect on the fracture strength of unidirectional continuous glass fiber reinforced polypropylene composites（unidirectional GF/PP composites）, the Zwick/Roell Z005 universal material testing machine was used to test different gauge lengths through orthogonal test methods.（60 mm, 100 mm, 200 mm）, unidirectional GF/PP composites with different widths（10 mm, 15 mm, 20 mm） are subjected to tensile test. The test results show that as the test size increases, the breaking strength of unidirectional GF/PP composites gradually decreases. Because the fracture strength of unidirectional GF/PP composites has a large dispersion, the distribution law of the strength of unidirectional GF/PP composites under different size conditions is obtained through the classic two-parameter Weibull strength statistical model, and the improved generalized The two-parameter weakest chain strength statistical model introduces the exponential parameterβto modify the influence of the spatial distribution of defects. The fracture strength data under different sizes are processed in a unified manner. The resulting failure function comprehensively reflects the size effect on the unidirectional GF/PP composite The effect of material breaking strength.
THE INFLUENCE OF SIZE EFFECT ON THE FRACTURE STRENGTH OF UNIDIRECTIONAL GLASS FIBER REINFORCED POLYPROPYLENE COMPOSITE
In order to explore the influence of the size effect on the fracture strength of unidirectional continuous glass fiber reinforced polypropylene composites（unidirectional GF/PP composites）, the Zwick/Roell Z005 universal material testing machine was used to test different gauge lengths through orthogonal test methods.（60 mm, 100 mm, 200 mm）, unidirectional GF/PP composites with different widths（10 mm, 15 mm, 20 mm） are subjected to tensile test. The test results show that as the test size increases, the breaking strength of unidirectional GF/PP composites gradually decreases. Because the fracture strength of unidirectional GF/PP composites has a large dispersion, the distribution law of the strength of unidirectional GF/PP composites under different size conditions is obtained through the classic two-parameter Weibull strength statistical model, and the improved generalized The two-parameter weakest chain strength statistical model introduces the exponential parameterβto modify the influence of the spatial distribution of defects. The fracture strength data under different sizes are processed in a unified manner. The resulting failure function comprehensively reflects the size effect on the unidirectional GF/PP composite The effect of material breaking strength.
THE INFLUENCE OF SIZE EFFECT ON THE FRACTURE STRENGTH OF UNIDIRECTIONAL GLASS FIBER REINFORCED POLYPROPYLENE COMPOSITE
ZHU YuYang (author) / ZHAI JianGuang (author) / GAO Chun (author) / LU HuiQin (author)
2022
Article (Journal)
Electronic Resource
Unknown
Metadata by DOAJ is licensed under CC BY-SA 1.0
Vibration welding of a unidirectional continuous glass fiber reinforced polypropylene GMT
| British Library Online Contents | 2005
Fatigue mechanisms in unidirectional glass-fibre-reinforced polypropylene
| British Library Online Contents | 1999
Strength and Fracture of Unidirectional Green Composites Reinforced by Hemp Fiber
| British Library Online Contents | 2010
Size effect in fracture of unidirectional composite plates
| British Library Online Contents | 1999
GLS strength prediction of glass-fiber-reinforced polypropylene
| British Library Online Contents | 2009