Use of the small punch test for the estimation of ductile-to-brittle transition temperature shift of irradiated steels
The small punch test is evaluated as a screening procedure for irradiation embrittlement of reactor pressure vessel steels. In particular, the correlation between ductile-to-brittle transition temperatures obtained from this small specimen test technique and from the standard Charpy impact test is investigated. Small punch tests and Charpy impact tests at different temperatures were performed on various steels including materials from original reactor pressure vessels in the unirradiated, neutron irradiated and annealed condition. It is demonstrated that the small punch test is a reliable and effective supportive means for the estimation of the irradiation-induced shift of the ductile-to-brittle transition temperature. It was found that a tanh-fit of the normalized small punch energy in dependence of temperature is preferable in comparison to the two-curve fit of the total small punch energy.
Use of the small punch test for the estimation of ductile-to-brittle transition temperature shift of irradiated steels
The small punch test is evaluated as a screening procedure for irradiation embrittlement of reactor pressure vessel steels. In particular, the correlation between ductile-to-brittle transition temperatures obtained from this small specimen test technique and from the standard Charpy impact test is investigated. Small punch tests and Charpy impact tests at different temperatures were performed on various steels including materials from original reactor pressure vessels in the unirradiated, neutron irradiated and annealed condition. It is demonstrated that the small punch test is a reliable and effective supportive means for the estimation of the irradiation-induced shift of the ductile-to-brittle transition temperature. It was found that a tanh-fit of the normalized small punch energy in dependence of temperature is preferable in comparison to the two-curve fit of the total small punch energy.
Use of the small punch test for the estimation of ductile-to-brittle transition temperature shift of irradiated steels
E. Altstadt (author) / F. Bergner (author) / M. Houska (author)
2021
Article (Journal)
Electronic Resource
Unknown
Metadata by DOAJ is licensed under CC BY-SA 1.0
| British Library Online Contents | 2008
| British Library Online Contents | 2008
Brittle-Ductile Transition of Bridge Steels
NTIS | 1990
Ductile to Brittle Transition Temperature of Functionally Graded Steels
| British Library Online Contents | 2012
Brittle fracture initiation in low carbon steels at ductile-brittle transition temperature region
| British Library Online Contents | 1994