Corrosion characteristics of reduced activation ferritic-martensitic steel EUROFER by Li2TiO3 with excess Li
In a solid breeding blanket, ceramic breeder pebbles are in contact with reduced activation ferritic martensitic (RAFM) steel at high temperatures for years and accordingly form a corrosion layer on the blanket structural steel. Present study focuses on corrosion characteristics of EUROFER97 RAFM steel by an advanced breeder material of Li2TiO3 with excess Li (initial ratio of Li/Ti = 2.2) at 623, 823, and 1073 K under sweep gas (He + 0.1% H2) flow. Formation of a thick oxide double layer was found on the surface of the EUROFER plates heated at 823 and 1073 K, while the corrosion layer formed at 673 K was < 1 µm even after 56 days. On the other hand, the changes that appeared on the contacted surface of the breeder pellet were insignificant. The growth of the corrosion layer shows that the corrosion caused by inward migrations mainly of Li and O from the breeder material will have little influence on mechanical property of the blanket structural steel. Keywords: Corrosion, RAFM steel, Ceramic breeder, DEMO blanket, Compatibility
Corrosion characteristics of reduced activation ferritic-martensitic steel EUROFER by Li2TiO3 with excess Li
In a solid breeding blanket, ceramic breeder pebbles are in contact with reduced activation ferritic martensitic (RAFM) steel at high temperatures for years and accordingly form a corrosion layer on the blanket structural steel. Present study focuses on corrosion characteristics of EUROFER97 RAFM steel by an advanced breeder material of Li2TiO3 with excess Li (initial ratio of Li/Ti = 2.2) at 623, 823, and 1073 K under sweep gas (He + 0.1% H2) flow. Formation of a thick oxide double layer was found on the surface of the EUROFER plates heated at 823 and 1073 K, while the corrosion layer formed at 673 K was < 1 µm even after 56 days. On the other hand, the changes that appeared on the contacted surface of the breeder pellet were insignificant. The growth of the corrosion layer shows that the corrosion caused by inward migrations mainly of Li and O from the breeder material will have little influence on mechanical property of the blanket structural steel. Keywords: Corrosion, RAFM steel, Ceramic breeder, DEMO blanket, Compatibility
Corrosion characteristics of reduced activation ferritic-martensitic steel EUROFER by Li2TiO3 with excess Li
Keisuke Mukai (author) / Fernando Sanchez (author) / Tsuyoshi Hoshino (author) / Regina Knitter (author)
2018
Article (Journal)
Electronic Resource
Unknown
Metadata by DOAJ is licensed under CC BY-SA 1.0
| British Library Online Contents | 2013
Abnormal Grain Growth in Ferritic-Martensitic Eurofer-97 Steel
| British Library Online Contents | 2013
Annealing effects on microstructure and coercive field of ferritic-martensitic ODS Eurofer steel
| British Library Online Contents | 2011
| British Library Online Contents | 2012
Laser Beam Welding for Reduced Activation Ferritic/Martensitic Steel F82H
| British Library Online Contents | 2014