Change in Micromechanical Behavior of Surface Densified Wood Cell Walls in Response to Superheated Steam Treatment
The combination of surface densification and superheated steam treatment is an effective method to improve the mechanical properties and dimensional stability of low-density wood. The objective of the current work is to evaluate the effects of superheated steam treatment on the micromechanical behavior of surface densified wood. The microstructure, chemical composition, cellulose crystalline structure, and micromechanical behavior of surface densified wood under different superheated steam pressures were investigated. Results indicated that both 0.1 MPa and 0.3 MPa superheated steam treatments increased the elastic modulus and hardness of fiber cell walls in surface densified wood. However, the average creep ratio and maximum creep compliance J(50) of surface densified wood under 0.3 MPa decreased by 41.59% and 6.76%, respectively, compared with untreated wood. The improvement of elastic modulus, hardness and creep resistance of surface densified wood treated with superheated steam was associated with the increase of relative crystallinity (CrI) and crystalline size. In addition, 0.3 MPa superheated steam treatment displayed a better effect on the enhancement of the elastic modulus, hardness, and creep resistance of the fiber cell wall than 0.1 MPa superheated steam treatment.
Change in Micromechanical Behavior of Surface Densified Wood Cell Walls in Response to Superheated Steam Treatment
The combination of surface densification and superheated steam treatment is an effective method to improve the mechanical properties and dimensional stability of low-density wood. The objective of the current work is to evaluate the effects of superheated steam treatment on the micromechanical behavior of surface densified wood. The microstructure, chemical composition, cellulose crystalline structure, and micromechanical behavior of surface densified wood under different superheated steam pressures were investigated. Results indicated that both 0.1 MPa and 0.3 MPa superheated steam treatments increased the elastic modulus and hardness of fiber cell walls in surface densified wood. However, the average creep ratio and maximum creep compliance J(50) of surface densified wood under 0.3 MPa decreased by 41.59% and 6.76%, respectively, compared with untreated wood. The improvement of elastic modulus, hardness and creep resistance of surface densified wood treated with superheated steam was associated with the increase of relative crystallinity (CrI) and crystalline size. In addition, 0.3 MPa superheated steam treatment displayed a better effect on the enhancement of the elastic modulus, hardness, and creep resistance of the fiber cell wall than 0.1 MPa superheated steam treatment.
Change in Micromechanical Behavior of Surface Densified Wood Cell Walls in Response to Superheated Steam Treatment
Elin Xiang (author) / Rongfeng Huang (author) / Shumin Yang (author)
2021
Article (Journal)
Electronic Resource
Unknown
Metadata by DOAJ is licensed under CC BY-SA 1.0
Experimental micromechanical characterisation of wood cell walls
| British Library Online Contents | 2013
Micromorphological studies of surface densified wood
| British Library Online Contents | 2014