Moisture Dry-Out Capability of Steel-Faced Mineral Wool Insulated Sandwich Panels
Moisture dry-out from steel-faced insulated sandwich panels has previously received little attention from researchers. This paper reports the results from laboratory tests and dynamic heat, air, and moisture transport simulations of the moisture dry-out capabilities of a steel-faced sandwich panel with a mineral wool core. Three test walls (TWs) with dimensions of 1.2 m × 0.4 m × 0.23 m were put above water containers to examine the moisture transport through the TWs. A calibrated simulation model was used to investigate the hygrothermal regime of a sandwich panel wall enclosure with different initial moisture contents and panel joint tightening tapes. The moisture dry-out capacity of the studied sandwich panels is limited (up to 2 g/day through a 30-mm-wide and 3-m-long vertical joint without tapes). When the vertical joint was covered with a vapour-permeable tape, the moisture dry-out was reduced to 1 g/day and when the joint was covered with a vapour-retarding tape, the dry-out was negligible. A very small amount of rain would be enough to raise the moisture content to water vapour saturation levels inside the sandwich wall, had the rain ingressed the enclosure. The calculated time of wetness (TOW) on the internal surface of the outer steel sheet stayed indefinitely at about 5500 h/year when vapour-retarding tapes were used and the initial relative humidity (RH) was over 80%. TOW stabilised to about 2000 h/year when a vapour-permeable tape was used regardless of the initial humidity inside the panel. A vapour-permeable tape allowed moisture dry-out but also vapour diffusion from the outside environment. To minimise the risk of moisture damage, avoiding moisture ingress during construction time or due to accidents is necessary. Additionally, a knowledge-based method is recommended to manage moisture safety during the construction process.
Moisture Dry-Out Capability of Steel-Faced Mineral Wool Insulated Sandwich Panels
Moisture dry-out from steel-faced insulated sandwich panels has previously received little attention from researchers. This paper reports the results from laboratory tests and dynamic heat, air, and moisture transport simulations of the moisture dry-out capabilities of a steel-faced sandwich panel with a mineral wool core. Three test walls (TWs) with dimensions of 1.2 m × 0.4 m × 0.23 m were put above water containers to examine the moisture transport through the TWs. A calibrated simulation model was used to investigate the hygrothermal regime of a sandwich panel wall enclosure with different initial moisture contents and panel joint tightening tapes. The moisture dry-out capacity of the studied sandwich panels is limited (up to 2 g/day through a 30-mm-wide and 3-m-long vertical joint without tapes). When the vertical joint was covered with a vapour-permeable tape, the moisture dry-out was reduced to 1 g/day and when the joint was covered with a vapour-retarding tape, the dry-out was negligible. A very small amount of rain would be enough to raise the moisture content to water vapour saturation levels inside the sandwich wall, had the rain ingressed the enclosure. The calculated time of wetness (TOW) on the internal surface of the outer steel sheet stayed indefinitely at about 5500 h/year when vapour-retarding tapes were used and the initial relative humidity (RH) was over 80%. TOW stabilised to about 2000 h/year when a vapour-permeable tape was used regardless of the initial humidity inside the panel. A vapour-permeable tape allowed moisture dry-out but also vapour diffusion from the outside environment. To minimise the risk of moisture damage, avoiding moisture ingress during construction time or due to accidents is necessary. Additionally, a knowledge-based method is recommended to manage moisture safety during the construction process.
Moisture Dry-Out Capability of Steel-Faced Mineral Wool Insulated Sandwich Panels
Kristo Kalbe (author) / Hubert Piikov (author) / Targo Kalamees (author)
2020
Article (Journal)
Electronic Resource
Unknown
Metadata by DOAJ is licensed under CC BY-SA 1.0
Improved Stone Wool Core for Metal Faced Building Sandwich Panels
| British Library Conference Proceedings | 1998
Structural Evaluation of Steel Faced Sandwich Panels
| NTIS | 1972
Structural evaluation of steel faced sandwich panels
| TIBKAT | 1974
Metal-faced sandwich composite panels: A review
| Elsevier | 2023