Internal cracking of fillet welds in thick sheets
Tests revealed that cracks occurred only in layer of 2 mm thickness, 1.5 mm below surface; how quality of material affects cracking. (Supplement to Bautechnik)
Internal cracking of fillet welds in thick sheets
Tests revealed that cracks occurred only in layer of 2 mm thickness, 1.5 mm below surface; how quality of material affects cracking. (Supplement to Bautechnik)
Internal cracking of fillet welds in thick sheets
Innere Rissbildung in Kehlnahtschweissungen bei Verwendung groesserer Blechdicken
Wegerhoff, E. (author)
Stahlbau ; 22
1953
4 pages
Article (Journal)
English
© Metadata Copyright Elsevier B. V. All rights reserved.
Early Development of Fatigue Cracking at Manual Fillet Welds
| British Library Online Contents | 1996
Elsevier | 1987
Reinforcing fillet welds preventing cracks in partial joint penetration welds
| Springer Verlag | 2015
Reinforcing fillet welds preventing cracks in partial joint penetration welds
| Online Contents | 2015
Fatigue Analysis of Load-Carrying Fillet Welds
| Online Contents | 2006