Results of Swiss tests on embrittlement phenomenon occurring in ductile steels, in particular at concave side of cold bends made in reinforcing bars; steel on inside of bend undergoes plastic deformation in compression, which may result in resi dual internal tensile stresses causing formation of crack. Before Int. Congress on Concrete.
Results of Swiss tests on embrittlement phenomenon occurring in ductile steels, in particular at concave side of cold bends made in reinforcing bars; steel on inside of bend undergoes plastic deformation in compression, which may result in resi dual internal tensile stresses causing formation of crack. Before Int. Congress on Concrete.
Cracking of reinforcing bars at cold bends
Civil Eng. (N. Y.)
Wyss, T. (author)
1931
3 pages
5 Figs.
Article (Journal)
English
© Metadata Copyright Elsevier B. V. All rights reserved.
Repair device for exposed reinforcing bars during concrete cracking
| European Patent Office | 2023
Early-age Cracking Control on Concrete with Reinforcing Bars
| Springer Verlag | 2024
Corrosion-Induced Concrete Cracking for Uncoated and Galvanized Reinforcing Bars
| British Library Online Contents | 2018
Bond characteristics of cold-twisted square steel reinforcing bars
| Engineering Index Backfile | 1959
Engineering Index Backfile | 1931