Long-time creep relaxation tests on high-tensile steel prestressing wire
Test was performed on two wires simultaneously and was carried on for 4 yr; material tested was cold-drawn prestressing wire, 7 mm in diam, which had 0.2% offset limit of about 155 kg/ sq mm and ultimate tensile strength of about 175 kg/sq mm; testing was made at constant temperature of 21 plus or minus 1 C in creep testing machine built in laboratory; machine comprised two separate testing sections and consisted of balance where wires were loaded by weights through lever; test results. In Swedish with English Summary.
Long-time creep relaxation tests on high-tensile steel prestressing wire
Test was performed on two wires simultaneously and was carried on for 4 yr; material tested was cold-drawn prestressing wire, 7 mm in diam, which had 0.2% offset limit of about 155 kg/ sq mm and ultimate tensile strength of about 175 kg/sq mm; testing was made at constant temperature of 21 plus or minus 1 C in creep testing machine built in laboratory; machine comprised two separate testing sections and consisted of balance where wires were loaded by weights through lever; test results. In Swedish with English Summary.
Long-time creep relaxation tests on high-tensile steel prestressing wire
Kryprelaxationsprov med hoghallfast forspanningstrad under lang tid
Engberg, E. (author) / Wallin, L. (author)
1966
6 pages
Article (Journal)
English
© Metadata Copyright Elsevier B. V. All rights reserved.
Some relaxation tests on prestressing wire
| Engineering Index Backfile | 1958
Thermal creep and relaxation of prestressing steel
| Online Contents | 2016
Thermal creep and relaxation of prestressing steel
| Elsevier | 2016
Thermal creep and relaxation of prestressing steel
| British Library Online Contents | 2016
Thermal creep and relaxation of prestressing steel
| British Library Online Contents | 2016