Investigation of mild steel corrosion rate in San Diego Harbor
Mild steel panels exposed for 6, 12 and 18 mo; basic corrosion rate for unprotected panels over 1 yr exposure was 25.8 mdd and greatest pit depth found exceeded 60 tho\ill\dths of in.; fully protected panels suffered virtually no corrosion while partially protected panels had corrosion rate of 8.3 mdd; greatest pit depth found on partially protected panels was only 9 mils.
Investigation of mild steel corrosion rate in San Diego Harbor
Mild steel panels exposed for 6, 12 and 18 mo; basic corrosion rate for unprotected panels over 1 yr exposure was 25.8 mdd and greatest pit depth found exceeded 60 tho\ill\dths of in.; fully protected panels suffered virtually no corrosion while partially protected panels had corrosion rate of 8.3 mdd; greatest pit depth found on partially protected panels was only 9 mils.
Investigation of mild steel corrosion rate in San Diego Harbor
Corrosion
Peterson, M.H. (author) / Waldron, L.J. (author)
Corrosion ; 17
1961
3 pages
Article (Journal)
English
© Metadata Copyright Elsevier B. V. All rights reserved.
Harbor of sun -- San Diego, Calif.
| Engineering Index Backfile | 1941
The Role of Flow Rate on Mild Steel Corrosion
British Library Online Contents | 1991
San Diego: Port of San Diego and Army Corps of Engineers begin Harbor Dredging Project
British Library Online Contents | 2004
Investigation of Pseudo-Passivation of Mild Steel in CO~2 Corrosion
| British Library Online Contents | 2014
Investigation on some Schiff bases as corrosion inhibitors for mild steel
| British Library Online Contents | 2006