Fracture of case hardened steel parts
Experimental data are interpreted to show that carburized case under load causes state of multiaxial embrittling stress at case core interface; existence of this state of stress is responsible for crack formation; ability of material of core to deform plastically under this stress determines crack propagation.
Fracture of case hardened steel parts
Experimental data are interpreted to show that carburized case under load causes state of multiaxial embrittling stress at case core interface; existence of this state of stress is responsible for crack formation; ability of material of core to deform plastically under this stress determines crack propagation.
Fracture of case hardened steel parts
Das Bruchverhalten einsatzgehaerteter Teile
Ebert, L.J. (author) / Krotine, F.T. (author) / Troiano, A.R. (author)
1967
8 pages
Article (Journal)
German
© Metadata Copyright Elsevier B. V. All rights reserved.
New method to evaluate fracture toughness of case-hardened steel
| British Library Online Contents | 1995
New method to evaluate fracture toughness of case-hardened steel
| British Library Online Contents | 1995
Fracture analysis of a steel sandwich with hardened core
| British Library Online Contents | 1994
Thermal and Metallurgical Modelling of Laser Transformation Hardened Steel Parts
| British Library Online Contents | 2007
Peculiarities of Fatigue Fracture of Steel Hardened by Various Surface Treatments
| British Library Online Contents | 2013