Effect of secondary processing on the microstructure and wear behavior of spray formed Al–30Mg2Si–2Cu alloy
Graphical abstract Display Omitted Highlights ► The microstructure of spray formed Al–30Mg2Si–2Cu alloy has been finely refined. ► The effect of secondary processing on spray formed alloy has been investigated. ► Aging improved the wear resistance of spray formed Al–30Mg2Si–2Cu alloy. ► Hardness of age hardened spray formed alloy is higher than that of as-cast alloy.
Abstract In the present work, Al–30Mg2Si–2Cu alloy has been spray formed and subsequently hot pressed for densification. The alloy is then subjected to solutionizing and isothermal aging treatments. The microstructural features, hardness and wear behavior of spray formed and secondary processed alloys have been evaluated individually and compared with that of as-cast alloy. The microstructure of spray formed alloy showed refined and globular shaped primary Mg2Si intermetallic particles and Al2Cu precipitate particles uniformly distributed in Al matrix. The microstructure was refined further after hot consolidation. The microstructure after solution heat treatment appeared similar to that of the spray formed alloy but aging led to a further refinement in the microstructure compared to that of the hot pressed alloy. The evaluation of wear behavior of these alloys, under dry sliding condition, showed that the age hardened alloy exhibits maximum wear resistance and minimum coefficient of friction over the entire range of applied load (10–50N) at a sliding speed of 2ms−1 followed by hot pressed, spray formed and solution heat treated alloys. The as-cast alloy showed the least wear resistance and highest coefficient of friction. Similar trend has been observed even in their hardness values too. The wear resistance of the alloys is discussed in light of their microstructural modifications induced during spray forming and subsequent secondary processing and also the topography of worn surfaces.
Effect of secondary processing on the microstructure and wear behavior of spray formed Al–30Mg2Si–2Cu alloy
Graphical abstract Display Omitted Highlights ► The microstructure of spray formed Al–30Mg2Si–2Cu alloy has been finely refined. ► The effect of secondary processing on spray formed alloy has been investigated. ► Aging improved the wear resistance of spray formed Al–30Mg2Si–2Cu alloy. ► Hardness of age hardened spray formed alloy is higher than that of as-cast alloy.
Abstract In the present work, Al–30Mg2Si–2Cu alloy has been spray formed and subsequently hot pressed for densification. The alloy is then subjected to solutionizing and isothermal aging treatments. The microstructural features, hardness and wear behavior of spray formed and secondary processed alloys have been evaluated individually and compared with that of as-cast alloy. The microstructure of spray formed alloy showed refined and globular shaped primary Mg2Si intermetallic particles and Al2Cu precipitate particles uniformly distributed in Al matrix. The microstructure was refined further after hot consolidation. The microstructure after solution heat treatment appeared similar to that of the spray formed alloy but aging led to a further refinement in the microstructure compared to that of the hot pressed alloy. The evaluation of wear behavior of these alloys, under dry sliding condition, showed that the age hardened alloy exhibits maximum wear resistance and minimum coefficient of friction over the entire range of applied load (10–50N) at a sliding speed of 2ms−1 followed by hot pressed, spray formed and solution heat treated alloys. The as-cast alloy showed the least wear resistance and highest coefficient of friction. Similar trend has been observed even in their hardness values too. The wear resistance of the alloys is discussed in light of their microstructural modifications induced during spray forming and subsequent secondary processing and also the topography of worn surfaces.
Effect of secondary processing on the microstructure and wear behavior of spray formed Al–30Mg2Si–2Cu alloy
Goudar, Dayanand M. (author) / Raju, K. (author) / Srivastava, V.C. (author) / Rudrakshi, G.B. (author)
2012-11-03
8 pages
Article (Journal)
Electronic Resource
English
| British Library Online Contents | 2013
Microstructure and wear properties of spray formed Zn-38Al-2Cu alloy
| British Library Online Contents | 2009
| British Library Online Contents | 2002
Shape, microstructure and wear of spray formed hypoeutectic Al-Si alloys
| British Library Online Contents | 2008
Microstructure and wear resistance of spray formed high chromium white cast iron
| British Library Online Contents | 2004