Hot workability of 00Cr13Ni5Mo2 supermartensitic stainless steel
Highlights ► The hot compression and hot tension tests for 00Cr13Ni5Mo2 supermartensitic stainless steel were conducted in the temperature range of 950–1200°C and strain rates varying between 0.1 and 50s[−1]. ► The processing maps at strains of 0.45 and 0.9 were constructed on the basis of dynamic materials model and Prasad instability criterion, respectively. ► The changes in hot deformation activation energy and Z−parameter at different working conditions were revealed. ►The optimum hot processing window was proposed for the industrial production.
Abstract The hot workability of 00Cr13Ni5Mo2 supermartensitic stainless steel was investigated by hot compression and hot tension tests conducted over the temperature range of 950–1200°C and strain rates varying between 0.1 and 50s−1. The processing map technique was applied on the basis of dynamic materials model and Prasad instability criterion. Microstructure evolutions, Zener–Hollomon parameter as well as hot tensile ductility were examined. The results show that, as for the hot working of 00Cr13Ni5Mo2 supermartensitic stainless steel in the industrial production, the large strain deformation should be carried out in the temperature range 1140–1200°C and strain rate range 0.1–50s−1, where the corresponding Zener–Hollomon parameters exhibit low values. Moreover, when deformed under high strain rate range (above 15s−1), the deformation temperature can be reduced reasonably.
Hot workability of 00Cr13Ni5Mo2 supermartensitic stainless steel
Highlights ► The hot compression and hot tension tests for 00Cr13Ni5Mo2 supermartensitic stainless steel were conducted in the temperature range of 950–1200°C and strain rates varying between 0.1 and 50s[−1]. ► The processing maps at strains of 0.45 and 0.9 were constructed on the basis of dynamic materials model and Prasad instability criterion, respectively. ► The changes in hot deformation activation energy and Z−parameter at different working conditions were revealed. ►The optimum hot processing window was proposed for the industrial production.
Abstract The hot workability of 00Cr13Ni5Mo2 supermartensitic stainless steel was investigated by hot compression and hot tension tests conducted over the temperature range of 950–1200°C and strain rates varying between 0.1 and 50s−1. The processing map technique was applied on the basis of dynamic materials model and Prasad instability criterion. Microstructure evolutions, Zener–Hollomon parameter as well as hot tensile ductility were examined. The results show that, as for the hot working of 00Cr13Ni5Mo2 supermartensitic stainless steel in the industrial production, the large strain deformation should be carried out in the temperature range 1140–1200°C and strain rate range 0.1–50s−1, where the corresponding Zener–Hollomon parameters exhibit low values. Moreover, when deformed under high strain rate range (above 15s−1), the deformation temperature can be reduced reasonably.
Hot workability of 00Cr13Ni5Mo2 supermartensitic stainless steel
Zou, Dening (author) / Han, Ying (author) / Yan, Dongna (author) / Wang, Duo (author) / Zhang, Wei (author) / Fan, Guangwei (author)
2011-03-26
6 pages
Article (Journal)
Electronic Resource
English
Hot workability of 00Cr13Ni5Mo2 supermartensitic stainless steel
| British Library Online Contents | 2011
Anodic behaviour of supermartensitic stainless steel weldments
| British Library Online Contents | 2010
Plasma nitriding of HP13Cr supermartensitic stainless steel
| British Library Online Contents | 2015
Intergranular corrosion susceptibility in supermartensitic stainless steel weldments
| British Library Online Contents | 2009
Titanium and molybdenum content in supermartensitic stainless steel
| British Library Online Contents | 2007