Theoretical and experimental study of microcell and macrocell corrosion in patch repairs of concrete structures
AbstractPatch repair is commonly used to rectify localized corrosion induced damage in concrete structures. However, inadequate durability in patch repair systems caused by new corrosion attack is prevalent. From the prevailing understanding, the mechanism is attributed to macrocell corrosion formed between repaired area (called patch) and its adjacent unrepaired area (called substrate), and thereby ensuring electrochemical compatibility between the two areas is deemed to be the key element to reduce the corrosion risk and thus to achieve a successful repair. This paper examined the corrosion mechanism and the concept of compatibility in patch repair systems from fundamental electrochemical principles and experimental verification. It was illustrated that both macrocell and microcell corrosion mechanisms could play significant roles, and the total corrosion could be underestimated if the latter is overlooked. Although the incompatibility serves as the driving force for the macrocell corrosion, in light of corrosion kinetics, it was shown that the corrosion magnitude depends more on the individual corrosion kinetics of the anode or cathode.
Theoretical and experimental study of microcell and macrocell corrosion in patch repairs of concrete structures
AbstractPatch repair is commonly used to rectify localized corrosion induced damage in concrete structures. However, inadequate durability in patch repair systems caused by new corrosion attack is prevalent. From the prevailing understanding, the mechanism is attributed to macrocell corrosion formed between repaired area (called patch) and its adjacent unrepaired area (called substrate), and thereby ensuring electrochemical compatibility between the two areas is deemed to be the key element to reduce the corrosion risk and thus to achieve a successful repair. This paper examined the corrosion mechanism and the concept of compatibility in patch repair systems from fundamental electrochemical principles and experimental verification. It was illustrated that both macrocell and microcell corrosion mechanisms could play significant roles, and the total corrosion could be underestimated if the latter is overlooked. Although the incompatibility serves as the driving force for the macrocell corrosion, in light of corrosion kinetics, it was shown that the corrosion magnitude depends more on the individual corrosion kinetics of the anode or cathode.
Theoretical and experimental study of microcell and macrocell corrosion in patch repairs of concrete structures
Qian, Shiyuan (author) / Zhang, Jieying (author) / Qu, Deyu (author)
Cement and Concrete Composites ; 28 ; 685-695
2006-01-01
11 pages
Article (Journal)
Electronic Resource
English
Macrocell Corrosion Formation in Concrete Patch Repairs - A Laboratory Study
| British Library Conference Proceedings | 2016
Macrocell and Microcell Corrosion of Embedded Steels in Concrete with Chloride Ions
| British Library Conference Proceedings | 1996