A ternary optimization of alkali-activated cement mortars incorporating glass powder, slag and calcium aluminate cement
https://orcid.org/0000-0002-9120-8864
Highlights The optimal ratios of GP, GGBS and CAC in AAC mortars using GC as aggregate were obtained. The effect of ternary binders on the mechanical property and durability was investigated. The performance prediction equations of the ternary composite mortars were obtained.
Abstract This paper introduces the use of a simplex-centroid design method, together with a ternary contour diagram, to evaluate the effect of blending different proportions of soda lime glass powder (GP), ground granulated blast furnace slag (GGBS) and calcium aluminate cement (CAC) on the compressive strength, alkali-silica reaction (ASR) expansion, drying shrinkage and high temperature resistance of alkali-activated cement (AAC) mortars prepared with the use of crushed glass cullet (GC) as aggregates. The relationship between performance of the geopolymer and precursor composition was established. It was found the ASR expansion increased with the increase of GP content and the addition of CAC as the replacement of GGBS could significantly reduce the ASR expansion. The drying shrinkage increased with the increase of GGBS contents. The residual strength coefficient of the mortars after high temperature exposure increased with the increase of CAC content and could be higher than 100%. And the strength coefficient increased with the increase of GP content resulted from its partial melting at the high temperature. It was found that the GP content should be in the range of 77–90%, the GGBS content should be lower than 5% and the CAC content should be higher than 10% to achieve acceptable ASR expansion and drying shrinkage.
A ternary optimization of alkali-activated cement mortars incorporating glass powder, slag and calcium aluminate cement
https://orcid.org/0000-0002-9120-8864
Highlights The optimal ratios of GP, GGBS and CAC in AAC mortars using GC as aggregate were obtained. The effect of ternary binders on the mechanical property and durability was investigated. The performance prediction equations of the ternary composite mortars were obtained.
Abstract This paper introduces the use of a simplex-centroid design method, together with a ternary contour diagram, to evaluate the effect of blending different proportions of soda lime glass powder (GP), ground granulated blast furnace slag (GGBS) and calcium aluminate cement (CAC) on the compressive strength, alkali-silica reaction (ASR) expansion, drying shrinkage and high temperature resistance of alkali-activated cement (AAC) mortars prepared with the use of crushed glass cullet (GC) as aggregates. The relationship between performance of the geopolymer and precursor composition was established. It was found the ASR expansion increased with the increase of GP content and the addition of CAC as the replacement of GGBS could significantly reduce the ASR expansion. The drying shrinkage increased with the increase of GGBS contents. The residual strength coefficient of the mortars after high temperature exposure increased with the increase of CAC content and could be higher than 100%. And the strength coefficient increased with the increase of GP content resulted from its partial melting at the high temperature. It was found that the GP content should be in the range of 77–90%, the GGBS content should be lower than 5% and the CAC content should be higher than 10% to achieve acceptable ASR expansion and drying shrinkage.
A ternary optimization of alkali-activated cement mortars incorporating glass powder, slag and calcium aluminate cement
https://orcid.org/0000-0002-9120-8864
Highlights The optimal ratios of GP, GGBS and CAC in AAC mortars using GC as aggregate were obtained. The effect of ternary binders on the mechanical property and durability was investigated. The performance prediction equations of the ternary composite mortars were obtained.
Abstract This paper introduces the use of a simplex-centroid design method, together with a ternary contour diagram, to evaluate the effect of blending different proportions of soda lime glass powder (GP), ground granulated blast furnace slag (GGBS) and calcium aluminate cement (CAC) on the compressive strength, alkali-silica reaction (ASR) expansion, drying shrinkage and high temperature resistance of alkali-activated cement (AAC) mortars prepared with the use of crushed glass cullet (GC) as aggregates. The relationship between performance of the geopolymer and precursor composition was established. It was found the ASR expansion increased with the increase of GP content and the addition of CAC as the replacement of GGBS could significantly reduce the ASR expansion. The drying shrinkage increased with the increase of GGBS contents. The residual strength coefficient of the mortars after high temperature exposure increased with the increase of CAC content and could be higher than 100%. And the strength coefficient increased with the increase of GP content resulted from its partial melting at the high temperature. It was found that the GP content should be in the range of 77–90%, the GGBS content should be lower than 5% and the CAC content should be higher than 10% to achieve acceptable ASR expansion and drying shrinkage.
A ternary optimization of alkali-activated cement mortars incorporating glass powder, slag and calcium aluminate cement
He, Pingping (author) / Zhang, Binyu (author) / Lu, Jian-Xin (author) / Poon, Chi Sun (author)
2019-12-28
Article (Journal)
Electronic Resource
English
Alkali-activated blends of calcium aluminate cement and slag/diatomite
| Tema Archive | 2013
Petrographical analysis of calcium aluminate cement mortars
| Online Contents | 1999
Alkali-silica reaction in calcium aluminate cement mortars induced by deicing salts solutions
| Taylor & Francis Verlag | 2022