Synthesis and characterization of polyurethane-coated palygorskite
AbstractPalygorskite was coated with polyurethane latex with aluminium potassium sulfate dodecahydrate as demulsifying agent. The coating was proofed by Fourier transform infrared (FTIR), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TG) and transmission electron microscopy (TEM). The thermogravimetric analysis indicated that the mass content of polyurethane was 9%. Transmission electron microscopy observation revealed that the coating was about 10nm thick.
Synthesis and characterization of polyurethane-coated palygorskite
AbstractPalygorskite was coated with polyurethane latex with aluminium potassium sulfate dodecahydrate as demulsifying agent. The coating was proofed by Fourier transform infrared (FTIR), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TG) and transmission electron microscopy (TEM). The thermogravimetric analysis indicated that the mass content of polyurethane was 9%. Transmission electron microscopy observation revealed that the coating was about 10nm thick.
Synthesis and characterization of polyurethane-coated palygorskite
Shi, Jianshe (author) / Yang, Xujie (author) / Han, Qiaofeng (author) / Wang, Xin (author) / Lu, Lude (author)
Applied Clay Science ; 46 ; 333-335
2009-09-07
3 pages
Article (Journal)
Electronic Resource
English
Synthesis and characterization of polyurethane-coated palygorskite
| Online Contents | 2009
Synthesis and characterization of polyurethane-coated palygorskite
| Online Contents | 2009
Synthesis and characterization of ZnO/palygorskite
| Elsevier | 2010