Synthetic zeolite pellets incorporated to air lime–metakaolin mortars: Mechanical properties
https://orcid.org/0000-0003-4717-6305
Highlights Synthetic fine and coarse zeolite pellets were added to air lime–metakaolin mortars. Synthetic zeolite pellets promote the development of pozzolanic phases. With the curing age both fine and coarse zeolite pellets improve mechanical strengths.
Abstract In this study synthetic fine and coarse zeolite pellets were chosen in the development of air lime–metakaolin mortars for repairing ancient masonry to be used in conservation and restoration of cultural heritage. Synthetic zeolite was used due to their particular water adsorption properties and act as an artificial pozzolan promoting the development of hydraulic phases. Physical, chemical, mineralogical and microstructural tests were accomplished to characterize the materials used in mortars’ preparation. Flexural, compressive strength and dynamic modulus of elasticity tests were performed in mortars at 28, 90 and 180days of curing. Incorporation of both fine and coarse zeolite pellets caused improvement of mechanical strength of mortars. The highest flexural strength value (∼0.5MPa) was achieved in both mortars with fine zeolites pellets at 90days and 20 and 30wt.% metakaolin, and coarse zeolite pellets at 180days and 30wt.% metakaolin as lime replacement. 1.0MPa was the highest compressive strength value obtained at 180days for mortars with both fine zeolite pellets and coarse zeolite pellets, with 20 and 30wt.% of metakaolin, respectively. Elasticity modulus ranged from 2.3GPa to 3.9GPa confirming the high deformation capability of these mortars. Zeolite pellets type A is a promise synthetic material that could be successfully used in air lime–metakaolin render mortars for applications in the conservation and restoration of cultural heritage.
Synthetic zeolite pellets incorporated to air lime–metakaolin mortars: Mechanical properties
https://orcid.org/0000-0003-4717-6305
Highlights Synthetic fine and coarse zeolite pellets were added to air lime–metakaolin mortars. Synthetic zeolite pellets promote the development of pozzolanic phases. With the curing age both fine and coarse zeolite pellets improve mechanical strengths.
Abstract In this study synthetic fine and coarse zeolite pellets were chosen in the development of air lime–metakaolin mortars for repairing ancient masonry to be used in conservation and restoration of cultural heritage. Synthetic zeolite was used due to their particular water adsorption properties and act as an artificial pozzolan promoting the development of hydraulic phases. Physical, chemical, mineralogical and microstructural tests were accomplished to characterize the materials used in mortars’ preparation. Flexural, compressive strength and dynamic modulus of elasticity tests were performed in mortars at 28, 90 and 180days of curing. Incorporation of both fine and coarse zeolite pellets caused improvement of mechanical strength of mortars. The highest flexural strength value (∼0.5MPa) was achieved in both mortars with fine zeolites pellets at 90days and 20 and 30wt.% metakaolin, and coarse zeolite pellets at 180days and 30wt.% metakaolin as lime replacement. 1.0MPa was the highest compressive strength value obtained at 180days for mortars with both fine zeolite pellets and coarse zeolite pellets, with 20 and 30wt.% of metakaolin, respectively. Elasticity modulus ranged from 2.3GPa to 3.9GPa confirming the high deformation capability of these mortars. Zeolite pellets type A is a promise synthetic material that could be successfully used in air lime–metakaolin render mortars for applications in the conservation and restoration of cultural heritage.
Synthetic zeolite pellets incorporated to air lime–metakaolin mortars: Mechanical properties
https://orcid.org/0000-0003-4717-6305
Highlights Synthetic fine and coarse zeolite pellets were added to air lime–metakaolin mortars. Synthetic zeolite pellets promote the development of pozzolanic phases. With the curing age both fine and coarse zeolite pellets improve mechanical strengths.
Abstract In this study synthetic fine and coarse zeolite pellets were chosen in the development of air lime–metakaolin mortars for repairing ancient masonry to be used in conservation and restoration of cultural heritage. Synthetic zeolite was used due to their particular water adsorption properties and act as an artificial pozzolan promoting the development of hydraulic phases. Physical, chemical, mineralogical and microstructural tests were accomplished to characterize the materials used in mortars’ preparation. Flexural, compressive strength and dynamic modulus of elasticity tests were performed in mortars at 28, 90 and 180days of curing. Incorporation of both fine and coarse zeolite pellets caused improvement of mechanical strength of mortars. The highest flexural strength value (∼0.5MPa) was achieved in both mortars with fine zeolites pellets at 90days and 20 and 30wt.% metakaolin, and coarse zeolite pellets at 180days and 30wt.% metakaolin as lime replacement. 1.0MPa was the highest compressive strength value obtained at 180days for mortars with both fine zeolite pellets and coarse zeolite pellets, with 20 and 30wt.% of metakaolin, respectively. Elasticity modulus ranged from 2.3GPa to 3.9GPa confirming the high deformation capability of these mortars. Zeolite pellets type A is a promise synthetic material that could be successfully used in air lime–metakaolin render mortars for applications in the conservation and restoration of cultural heritage.
Synthetic zeolite pellets incorporated to air lime–metakaolin mortars: Mechanical properties
Ferraz, Eduardo (author) / Andrejkovičová, Slávka (author) / Velosa, Ana L. (author) / Silva, António S. (author) / Rocha, Fernando (author)
Construction and Building Materials ; 69 ; 243-252
2014-07-15
10 pages
Article (Journal)
Electronic Resource
English
Synthetic zeolite pellets incorporated to air lime–metakaolin mortars: Mechanical properties
| British Library Online Contents | 2014
Synthetic zeolite pellets incorporated to air lime-metakaolin mortars: Mechanical properties
| British Library Online Contents | 2014
Synthetic zeolite pellets incorporated to air lime–metakaolin mortars: Mechanical properties
| BASE | 2014
Synthetic zeolite pellets incorporated to air lime–metakaolin mortars: Mechanical properties
| Online Contents | 2014