Experimental study on fatigue behavior of butt-welded thin-walled steel plates strengthened using CFRP sheets
Abstract Welded steel joints in structures are susceptible to fatigue failure. In this context, advanced carbon fiber reinforced polymer (CFRP) possess a demonstrated potential for the fatigue strengthening of steel structures. However, limited information is available on CFRP strengthening of butt-welded joints, which are the most common joint types in steel structures. This paper presents a study on fatigue behavior of butt-welded thin-walled steel plates strengthened using CFRP sheets. A total of 34 specimens with both single-sided and double-sided strengthening were performed via constant amplitude tensile fatigue loading, and another four specimens were employed for hot-spot stress measurement. The effect of CFRP strengthening on fatigue behavior was investigated by varying the strengthening scheme (single-sided or double-sided) and the number of CFRP sheet layers. Test results showed that the fatigue life of butt-welded steel plates with CFRP strengthening increased by approximately one to ten times when compared to the fatigue life of butt-welded steel plates without CFRP strengthening. Triple-layered double-sided specimens seemed to exhibit the best effect on fatigue life; their fatigue strength at 2 million cycles increased by 34% compared to that of specimens without CFRP strengthening. Specific fatigue design S–N curves of butt-welded thin-walled steel plates with and without CFRP strengthening were proposed directly. The fatigue test results were used to calibrate a fatigue design approach for CFRP strengthened butt-welded steel plates. In addition, the effect of CFRP strengthening on stiffness degradation was also discussed.
Highlights Thirty-four fatigue tests on CFRP strengthened butt-welded thin steel plates were conducted. Stress concentration factors for CFRP strengthened butt-welded steel plates were measured. Fatigue design approach for CFRP strengthened butt-welded steel plates was calibrated. The effect of CFRP strengthening on stiffness degradation was discussed.
Experimental study on fatigue behavior of butt-welded thin-walled steel plates strengthened using CFRP sheets
Abstract Welded steel joints in structures are susceptible to fatigue failure. In this context, advanced carbon fiber reinforced polymer (CFRP) possess a demonstrated potential for the fatigue strengthening of steel structures. However, limited information is available on CFRP strengthening of butt-welded joints, which are the most common joint types in steel structures. This paper presents a study on fatigue behavior of butt-welded thin-walled steel plates strengthened using CFRP sheets. A total of 34 specimens with both single-sided and double-sided strengthening were performed via constant amplitude tensile fatigue loading, and another four specimens were employed for hot-spot stress measurement. The effect of CFRP strengthening on fatigue behavior was investigated by varying the strengthening scheme (single-sided or double-sided) and the number of CFRP sheet layers. Test results showed that the fatigue life of butt-welded steel plates with CFRP strengthening increased by approximately one to ten times when compared to the fatigue life of butt-welded steel plates without CFRP strengthening. Triple-layered double-sided specimens seemed to exhibit the best effect on fatigue life; their fatigue strength at 2 million cycles increased by 34% compared to that of specimens without CFRP strengthening. Specific fatigue design S–N curves of butt-welded thin-walled steel plates with and without CFRP strengthening were proposed directly. The fatigue test results were used to calibrate a fatigue design approach for CFRP strengthened butt-welded steel plates. In addition, the effect of CFRP strengthening on stiffness degradation was also discussed.
Highlights Thirty-four fatigue tests on CFRP strengthened butt-welded thin steel plates were conducted. Stress concentration factors for CFRP strengthened butt-welded steel plates were measured. Fatigue design approach for CFRP strengthened butt-welded steel plates was calibrated. The effect of CFRP strengthening on stiffness degradation was discussed.
Experimental study on fatigue behavior of butt-welded thin-walled steel plates strengthened using CFRP sheets
Tong, Lewei (author) / Yu, Qitong (author) / Zhao, Xiao-Ling (author)
Thin-Walled Structures ; 147
2019-10-23
Article (Journal)
Electronic Resource
English
Fatigue Behavior of Cracked High-Strength Steel Plates Strengthened by CFRP Sheets
| Online Contents | 2016
Fatigue Behavior of Cracked High-Strength Steel Plates Strengthened by CFRP Sheets
| Online Contents | 2016
Fatigue strength of CFRP strengthened welded joints with corrugated steel plates
| British Library Online Contents | 2015