Novel Cu-bearing economical 21Cr duplex stainless steels
Highlights ► Cu-bearing DSSs had good corrosion resistance and low-temperature impact toughness. ► 21Cr-2 Ni-1.0Mo-0.2 N-1.0Cu showed excellent comprehensive properties. ► Sigma phase, ε-Cu and Cr2N were found when solution-treated at 780 °C for 30 min.
Abstract A new family of 21Cr–2Ni–1.0Mo–0.2N–xCu (x =0.5,1.0,1.5) economical duplex stainless steels have been developed by examining the effect of Cu on the microstructure and properties of solution-treated specimens. The results have shown that these alloys have a balanced ferrite–austenite duplex structure. The ferrite content increases with the solution treatment temperature, but decreases with an increase in Cu. Some precipitates such as sigma phase, ε-Cu and Cr2N were found when solution-treated at 780°C for 30min. The yield strength, tensile strength and fracture elongation values of experimental alloys solution-treated at 1020°C for 30min were about 540MPa, 1000MPa, and 35%, respectively. The pitting corrosion potentials of the solution-treated alloys were all above 500mV in 1mol/L NaCl solution at room temperature and the pitting corrosions always occur in ferrite phase. The mechanical properties and corrosion resistance of the designed alloys with lower production cost are better than those of AISI 316L austenitic stainless steel.
Novel Cu-bearing economical 21Cr duplex stainless steels
Highlights ► Cu-bearing DSSs had good corrosion resistance and low-temperature impact toughness. ► 21Cr-2 Ni-1.0Mo-0.2 N-1.0Cu showed excellent comprehensive properties. ► Sigma phase, ε-Cu and Cr2N were found when solution-treated at 780 °C for 30 min.
Abstract A new family of 21Cr–2Ni–1.0Mo–0.2N–xCu (x =0.5,1.0,1.5) economical duplex stainless steels have been developed by examining the effect of Cu on the microstructure and properties of solution-treated specimens. The results have shown that these alloys have a balanced ferrite–austenite duplex structure. The ferrite content increases with the solution treatment temperature, but decreases with an increase in Cu. Some precipitates such as sigma phase, ε-Cu and Cr2N were found when solution-treated at 780°C for 30min. The yield strength, tensile strength and fracture elongation values of experimental alloys solution-treated at 1020°C for 30min were about 540MPa, 1000MPa, and 35%, respectively. The pitting corrosion potentials of the solution-treated alloys were all above 500mV in 1mol/L NaCl solution at room temperature and the pitting corrosions always occur in ferrite phase. The mechanical properties and corrosion resistance of the designed alloys with lower production cost are better than those of AISI 316L austenitic stainless steel.
Novel Cu-bearing economical 21Cr duplex stainless steels
Ran, Qingxuan (author) / Li, Jun (author) / Xu, Yulai (author) / Xiao, Xueshan (author) / Yu, Haifeng (author) / Jiang, Laizhu (author)
2012-11-06
8 pages
Article (Journal)
Electronic Resource
English
Novel Cu-bearing economical 21Cr duplex stainless steels
| British Library Online Contents | 2013
| British Library Online Contents | 2013
| British Library Online Contents | 1993
Welding duplex and super duplex stainless steels
| British Library Online Contents | 1995