Development of wood-crete from treated sawdust
Highlights Hot water treatment resulted in significant improvement of wood-crete. Addition of NaOH was able to extract soluble content of sawdust. Linear correlation of waste paper reinforced wood-crete with boiling time of sawdust. Higher percentage of waste paper gave rise to a higher compressive strength. Geometry of waste paper had an influence on compressive strength of wood-crete.
Abstract The properties of wood-crete were investigated based on the modification of sawdust by hot water boiling, alkaline treatment and the addition of different types of waste paper. The results showed that (1) surface modification, processing of cellulosic fibril and the extraction of lignin and hemi-cellulosic compounds with alkali had an effect on the compressive strength of wood-crete, with treating sawdust with 4% NaOH at 140min of boiling time achieving the highest increase of 260% compressive strength; (2) boiling sawdust from 100min to 140min saw a gradual increase in compressive strength but reduced at a higher boiling time; (3) the combined effect of enhanced sawdust and addition of waste paper had a direct effect on the compressive strength of wood-crete with paper strip recording a much higher strength of 1.62MPa compared to 1.06MPa of de-fibred paper; (4) the treating sawdust with NaOH more than 4% weakened the individual wood particles thus leading to poor strength of wood-crete; and (5) water soaking resulted in a little water uptake (about 0.1%) of wood-crete whether with 1:1 or 1:2 sawdust to tradical lime ratio, but significant decrease in compressive strength, showing that the wood-crete could be used in damp areas only if it is not for load bearing purpose. The findings of this study provide an important background and foundation for achieving better strength of wood-crete and for directing a better uses of this potential low carbon sustainable product in construction.
Development of wood-crete from treated sawdust
Highlights Hot water treatment resulted in significant improvement of wood-crete. Addition of NaOH was able to extract soluble content of sawdust. Linear correlation of waste paper reinforced wood-crete with boiling time of sawdust. Higher percentage of waste paper gave rise to a higher compressive strength. Geometry of waste paper had an influence on compressive strength of wood-crete.
Abstract The properties of wood-crete were investigated based on the modification of sawdust by hot water boiling, alkaline treatment and the addition of different types of waste paper. The results showed that (1) surface modification, processing of cellulosic fibril and the extraction of lignin and hemi-cellulosic compounds with alkali had an effect on the compressive strength of wood-crete, with treating sawdust with 4% NaOH at 140min of boiling time achieving the highest increase of 260% compressive strength; (2) boiling sawdust from 100min to 140min saw a gradual increase in compressive strength but reduced at a higher boiling time; (3) the combined effect of enhanced sawdust and addition of waste paper had a direct effect on the compressive strength of wood-crete with paper strip recording a much higher strength of 1.62MPa compared to 1.06MPa of de-fibred paper; (4) the treating sawdust with NaOH more than 4% weakened the individual wood particles thus leading to poor strength of wood-crete; and (5) water soaking resulted in a little water uptake (about 0.1%) of wood-crete whether with 1:1 or 1:2 sawdust to tradical lime ratio, but significant decrease in compressive strength, showing that the wood-crete could be used in damp areas only if it is not for load bearing purpose. The findings of this study provide an important background and foundation for achieving better strength of wood-crete and for directing a better uses of this potential low carbon sustainable product in construction.
Development of wood-crete from treated sawdust
Aigbomian, Eboziegbe Patrick (author) / Fan, Mizi (author)
Construction and Building Materials ; 52 ; 353-360
2013-11-06
8 pages
Article (Journal)
Electronic Resource
English
Development of wood-crete from treated sawdust
| Online Contents | 2014
Development of wood-crete from treated sawdust
| British Library Online Contents | 2014
Development of Wood-Crete building materials from sawdust and waste paper
| Online Contents | 2013
Development of Wood-Crete building materials from sawdust and waste paper
| British Library Online Contents | 2013