Pozzolan obtained by mechanochemical and thermal treatments of kaolin
AbstractThis paper compares the pozzolanic activity of metakaolin (MK) obtained by thermal treatment at 700°C for 1h and amorphous kaolin obtained by mechanochemical treatment in a Herzog oscillating mill for 15–120min. The starting materials used included two raw kaolins and an industrial (washed) kaolin. The production of the amorphous materials was followed by their thermal analysis (DTA, TGA), X-ray diffraction (XRD), Fourier transform infrared spectrometry (FTIR), particle size distribution (PSD) and transmission electron microscopy (TEM). The pozzolanic activity of the amorphous kaolins was assessed in accordance with ASTM C 311. Based on the results, both types of treatment allow reactive pozzolans to be obtained from kaolinite clays. The pozzolan obtained by mechanochemical treatment of raw kaolin with high quartz content was found to perform especially well. In sample KV2, with a minor amount of kaolinite, it was possible to obtain an active pozzolan by mechanical treatment but not by thermal treatment. The pozzolanic index and the mechanical resistances obtained by grinding were similar to the thermal treatment. The outcome of the mechanochemical process depends on the type of kaolin used and its and mineralogical composition, and also on its grinding time.
Pozzolan obtained by mechanochemical and thermal treatments of kaolin
AbstractThis paper compares the pozzolanic activity of metakaolin (MK) obtained by thermal treatment at 700°C for 1h and amorphous kaolin obtained by mechanochemical treatment in a Herzog oscillating mill for 15–120min. The starting materials used included two raw kaolins and an industrial (washed) kaolin. The production of the amorphous materials was followed by their thermal analysis (DTA, TGA), X-ray diffraction (XRD), Fourier transform infrared spectrometry (FTIR), particle size distribution (PSD) and transmission electron microscopy (TEM). The pozzolanic activity of the amorphous kaolins was assessed in accordance with ASTM C 311. Based on the results, both types of treatment allow reactive pozzolans to be obtained from kaolinite clays. The pozzolan obtained by mechanochemical treatment of raw kaolin with high quartz content was found to perform especially well. In sample KV2, with a minor amount of kaolinite, it was possible to obtain an active pozzolan by mechanical treatment but not by thermal treatment. The pozzolanic index and the mechanical resistances obtained by grinding were similar to the thermal treatment. The outcome of the mechanochemical process depends on the type of kaolin used and its and mineralogical composition, and also on its grinding time.
Pozzolan obtained by mechanochemical and thermal treatments of kaolin
Vizcayno, C. (author) / de Gutiérrez, R.M. (author) / Castello, R. (author) / Rodriguez, E. (author) / Guerrero, C.E. (author)
Applied Clay Science ; 49 ; 405-413
2009-09-23
9 pages
Article (Journal)
Electronic Resource
English
Pozzolan obtained by mechanochemical and thermal treatments of kaolin
| Online Contents | 2010
MANUFACTURING PROCESS OF POZZOLAN WITH COLOR CHANGE AND POZZOLAN THUS OBTAINED
| European Patent Office | 2018
Manufacturing process of pozzolan with color change and pozzolan thus obtained
| European Patent Office | 2022
MANUFACTURING PROCESS OF POZZOLAN WITH COLOR CHANGE AND POZZOLAN THUS OBTAINED
| European Patent Office | 2021
MANUFACTURING PROCESS OF POZZOLAN WITH COLOR CHANGE AND POZZOLAN THUS OBTAINED
| European Patent Office | 2020