Cross-sectional TEM observation of iron–zinc intermetallic Γ and Γ1 phases in commercial galvannealed IF steel sheets
AbstractThe Γ phase and Γ1 phase in commercial galvannealed interstitial free (IF) steel sheets were studied by transmission electron microscopy (TEM). The cross-sectional TEM specimen was prepared using focused ion beam (FIB) technique which was also introduced briefly. The results show that there exist superlattice reflections in the selected diffraction patterns of both Γ phase and Γ1 phase, which indicate that both of the Γ phase and Γ1 phase are ordered intermetallic compounds. A Γ phase cell can be regarded as a α-Fe cell, which enlarges lattice constant three times in the x, y, z directions and keeps the same crystal structure with the Zn atoms occupying some positions of Fe atoms. A Γ1 phase can be formed by doubling the Γ phase cell in the x, y, z directions, while the crystal structure transforms from BCC to FCC.
Cross-sectional TEM observation of iron–zinc intermetallic Γ and Γ1 phases in commercial galvannealed IF steel sheets
AbstractThe Γ phase and Γ1 phase in commercial galvannealed interstitial free (IF) steel sheets were studied by transmission electron microscopy (TEM). The cross-sectional TEM specimen was prepared using focused ion beam (FIB) technique which was also introduced briefly. The results show that there exist superlattice reflections in the selected diffraction patterns of both Γ phase and Γ1 phase, which indicate that both of the Γ phase and Γ1 phase are ordered intermetallic compounds. A Γ phase cell can be regarded as a α-Fe cell, which enlarges lattice constant three times in the x, y, z directions and keeps the same crystal structure with the Zn atoms occupying some positions of Fe atoms. A Γ1 phase can be formed by doubling the Γ phase cell in the x, y, z directions, while the crystal structure transforms from BCC to FCC.
Cross-sectional TEM observation of iron–zinc intermetallic Γ and Γ1 phases in commercial galvannealed IF steel sheets
Yu, Jinshan (author) / Liu, Junliang (author) / Zhou, Weimin (author) / Zhang, Jinxu (author) / Wu, Jiansheng (author)
2005-04-28
5 pages
Article (Journal)
Electronic Resource
English
| British Library Online Contents | 2007
Cross-sectional observation of the intermetallic phase in a galvannealed steel
| British Library Online Contents | 2009
Electron diffraction study on iron–zinc Γ1 intermetallic phase in a galvannealed IF steel sheet
| British Library Online Contents | 2005
Influence Factors of Powdering-resistance of Galvannealed Steel Sheets
| British Library Online Contents | 2012
Corrosion-resistant Properties of Hot-dip Galvannealed Steel Sheets
| British Library Online Contents | 2009